Novel calcium hexaluminate/spinel-alumina composites with graded microstructures and mechanical properties

نویسندگان

  • Shuai Yi
  • Zhaohui Huang
  • Juntong Huang
  • Minghao Fang
  • Yan'gai Liu
  • Shaowei Zhang
چکیده

Calcium hexaluminate (CA6) was incorporated into the matrix of magnesio aluminate spinel-alumina (MA-A) via infiltration of a porous preform fabricated from α-Al2O3 and MgO powders with a saturated calcium acetate solution and subsequent firing, forming CA6/(MA-A) functionally composites with graded fracture toughness. Actually, the porous preform was partially and perpendicularly immersed (1/4 of its length) in the solution. Owing to the capillary action, the calcium acetate solution was absorbed into the porous preform, and the different absorption distance led to the graded solution concentration in the height direction of the porous preform. The in-situ formation of CA6 conferred graded microstructures, as well as improved mechanical properties on the resultant composites. The CA6 content decreased gradually along the solution absorption direction, i.e., from one end [CA6/(MA-A) region] immersed in solution to the other end [MA-A region], reducing evidently the formation of layered structure along the direction, while increasing gradually the formation of spherical alumina particles. The CA6/(MA-A) region had a better toughness that could prevent the crack propagation and improve the spalling resistance. Meanwhile, the MA-A region could provide structural support, because of the higher Vickers hardness and density.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

In-Situ Alumina/Aluminate Platelet Composites

Alumina composites containing in-situ-formed hexaluminate (LaAl,,018, LaMgAl,,O,,, SrAl12019, and Mg,NaAl,,O,) platelets can be pressureless-sintered to high density. The grain morphology of the aluminates can be controlled by composition. A peak toughness 50% higher than that of alumina is obtained at 30 vol% aluminates, with a modest reduction (10%) in hardness and Young’s modulus. Although c...

متن کامل

On the Study of Mechanical Properties of Aluminum/Nano-Alumina Composites Produced via Powder Injection Molding

Powder Injection Molding (PIM) is a precision manufacturing process used for production of advanced composites. Mixing of polymeric binder with metal powders, molding of feedstock, de-binding of brown parts and sintering of green samples are four main steps of this process. In the present study, the compounds containing multi-component binder system and aluminum/ nano-alumina (0-9 wt.%) powders...

متن کامل

Study of Mechanical Properties for the Aluminum Bronze Matrix Composites of Hot Pressing

The aluminum bronze matrix alumina composites using hot press and resin infiltration were investigated to study their porosities, hardness, bending strengths, and microstructures. The experiment results show that the hardness of the sintered composites with the decrease of porosity increases. The composites without and with resin infiltration have about HRF 42-61 of about 34-40% of porosity and...

متن کامل

Comparison of the effect of chromium oxide and magnesium oxide on the mechanical properties and microstructure of alumina-mullite-zirconia composites

Alumina-mullite-zirconia composites were prepared by the reaction sintering method between alumina and zircon powders and the effect of two additives (chromium oxide and manganese oxide)were investigated on their properties. 2 and 4 wt% of each oxide were added to the raw material composition and after pressing, the samples were sintered at 1630°C. The results showed that chromium oxide decreas...

متن کامل

COMMONALITY OF PHENOMENA IN COMPOSITE MATERIALS Polymer-bioceramic composites for tissue engineering scaffolds

Designing tissue engineering scaffolds with the required mechanical properties and favourable microstructure to promote cell attachment, growth and new tissue formation is one of the key challenges facing the tissue engineering field. An important class of scaffolds for bone tissue engineering is based on bioceramics and bioactive glasses, including: hydroxyapatite, bioactive glass (e.g. Biogla...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 4  شماره 

صفحات  -

تاریخ انتشار 2014