Effect of Cooling Rate on Morphology of TiAl3 Particles in Al–4Ti Master Alloy
نویسندگان
چکیده
The Al-4Ti master alloy was fabricated by aluminum (Al) and sponge titanium particle in a resistance furnace at different cooling rates. This work aims to investigate the relationship between the cooling rate and morphology of TiAl3. The microstructure and composition of master alloys at different cooling rates were characterized and analyzed by optical microscopy (OM), X-ray diffraction (XRD), differential scanning calorimetry (DSC), and SEM with energy dispersive spectroscopy (EDS). The results showed that various morphologies of TiAl3 particles in the Al-4Ti master alloy could be acquired at different cooling rates. Petal-like, blocky, and flake-like TiAl3 particles in the Al-4Ti master alloy were respectively acquired at the cooling rates of 3.36 K/s, 2.57 K/s, and 0.31 K/s. It was also found that the morphology of TiAl3 particles in the prepared master alloy changed from petal-like to blocky, then finally to flake-like, with the decrease of cooling rate. In addition, the morphology of the TiAl3 particles has no effect on the phase inversion temperature of Al-4Ti master alloy.
منابع مشابه
Grain Refinement Efficiency in Commercial-Purity Aluminum Influenced by the Addition of Al-4Ti Master Alloys with Varying TiAl3 Particles
A series of Al-4Ti master alloys with various TiAl₃ particles were prepared via pouring the pure aluminum added with K₂TiF₆ or sponge titanium into three different molds made of graphite, copper, and sand. The microstructure and morphology of TiAl₃ particles were characterized and analyzed by scanning electron microscope (SEM) with energy dispersive spectroscopy (EDS). The microstructure of TiA...
متن کاملMicrostructure and Grain Refining Performance of a New Al-Ti-C Master Alloy (RESEARCH NOTE)
Control of microstructure parameters that affecting the Al-Ti-C master alloys grain refining efficiency is leading to improve the aluminum grain refinement. This study was an attempt to produce Al-Ti-C master alloys that provide these controlling factors with relying on the solute effect theory. The produced master alloys were examined by using scanning electron microscopy (SEM), energy-dispers...
متن کاملEFFECT OF COOLING RATE AND GRAIN REFINEMENT ON THE MICROSEGREGATION IN Al-4.8 wt.% Cu ALLOY
Microsegregation is one of the most important phenomena occurs during solidification. It usually results in formation of some unexpected second phases which generally affect the mechanical properties and specially reduce the workability of casting products. The aim of this research is to study the effect of cooling rate and grain refinement on the microsegregation in Al-4.8 wt.% Cu. For this p...
متن کاملPulsed Nd:YAG Laser Dissimilar Welding of Grade 2 Titanium Alloy to 3105-O Aluminum Alloy using AlSi5 Filler Metal
A special form of laser spot welding is introduced to overlap dissimilar welding of titanium (G2) to 3105-O aluminum alloy. A welding tactile seam tracking design using following pulses that result to a circular seam leads to spot like shape laser welding. This technique was conducted to joint overlapped grad 2 Titanium alloy (Ti G2) to 3105-O Al alloy, with 1, and 0.5 mm thicknesses respective...
متن کاملEFFECT OF THE INCLINED COOLING PLATE CHARACTERISTICS ON THE THIXOTROPIC MICROSTRUCTURE OF A356.0 ALUMINUM ALLOY
In the present work microstructural evolution of A356 Aluminum alloy using an inclined cooling plate casting process for thixoforming feedstock production is investigated. The resultant microstructure was evaluated and compared with those of the same alloy produced by the conventional casting process, i.e. directly cast in the same mold without using an inclined cooling plate. It was found that...
متن کامل