Formation of glassy Ti50Cu20Ni24Si4B2 alloy by high-energy ball milling
نویسندگان
چکیده
The elemental powder mixtures with a nominal composition of Ti50Cu20Ni24Si4B2 can be amorphized under high-energy ball milling. A well-defined glass transition before crystallization appears in the obtained amorphous phase during heating in a differential scanning calorimeter. Awide supercooled liquid region DTx is available to be about 57 K. Crystallization of the ballmilled amorphous phase was performed through one step to form the metastable (Ni, Cu)Ti phase with cubic structure and an unknown phase, followed by subsequent grain growth. The reduced glass transition temperature of the alloy was determined to be
منابع مشابه
Glass formation in a (Ti,Zr,Hf)–(Cu,Ni,Ag)–Al high-order alloy system by mechanical alloying
In this work, glass formation under high-energy ball milling was investigated for a (Ti0.33Zr0.33Hf0.33)50(Ni0.33Cu0.33Ag0.33)40Al10 high-order alloy system with equiatomic substitution for early and late transition-metal contents. For comparison, an amorphous alloy ribbon with the same composition was prepared using the melt-spinning method as well. Structural features of the samples were char...
متن کاملFabrication of TiC particulate reinforced Ni-50Fe super alloy matrix composite powder by mechanical alloying
Mechanical alloying is a powder metallurgy processing technique involving cold welding, fracturing, and rewelding of powder particles in a high-energy ball mill. In this work, NiFe-TiC composite powders were prepared by mechanical alloying process using planetary high-energy ball mill. The effect of TiC addition by weight percent on the NiFe solid solution formation, grain size, lattice paramet...
متن کاملThe Influence of Heat Treatment and High Energy Ball Milling on the Density, Hardness, and Wear Behavior of Al 7150 Alloy via Hot Uniaxial Compaction
The effect of the milling time & ageing on the hardness, density, and wear characteristics of Al 7150 alloy specimens made via powder metallurgy has been studied. The different constituents of Al 7150 alloy were processed in a planetary ball milling set up with a BPR of 10:1 for 5 hours, 10 hours, and 20 hours. At 400 °C, the milled powders were subsequently hot compacted in a punch die setup. ...
متن کاملNano-Crystalline Mg(2-x)MnxNi Compounds Synthesized by Mechanical Alloying: Microstructure and Electrochemistry
Mechanical alloying of binary and ternary elemental powder mixtures with the nominal compositions of Mg2Ni and Mg(2-x)MnxNi (x= 0, 0.05, 0.10 and 0.15 at. %) were carried out in a planetary ball mill for various milling times of 5, 10, 15, 20, 30 and 60 h. X-ray diffraction and field emission scanning and transmission electron microscopy were used for the characterization of the milled products...
متن کاملMechano-chemical activation of MoO3-CuO/C powder mixture to synthesis nano crystalline Mo-Cu alloy
In this study, a high energy planetary ball milling technique was used to synthesize nano-crystalline Mo-Cu alloys. Molybdenum trioxide (MoO3) and copper oxide (CuO) were used as the starting materials. Carbo-thermal co-reduction of mixed Mo and Cu oxides powders was done with milling followed by a heat treatment at a high temperature. Differential thermal analysis/thermogravimetric (DTA/TG) wa...
متن کامل