A Novel Approach to Synthesis of FePt Magnetic Nanoparticles
نویسندگان
چکیده
Chemical reduction of ferric acetylacetonate (Fe(acac)3) and platinum acetylacetonate (Pt(acac)2) using polyol as a reducing agent as well as an effective surfactant, has successfully yielded monodisperse FePt nanoparticles with a size of approximately 2 nm. When annealed samples were compared to FePt nanoparticles synthesized using oleic acid and oleylamine as the surfactants under identical conditions, nearly 30% increase in coercivity (Hc) was achieved with the new, simple and economic method.
منابع مشابه
Synthesis and Morphology of Face Centered Cubic (FCC) Fe-Pt Nanoparticles
FePt nanoparticles with thermally stable room-temperature ferromagnetism are investigated. The monodisperse nanoparticles are prepared by chemical synthesis and a salt-matrix annealing technique. Structural and magnetic characterizations confirm the phase transition from the disordered face-centered cubic structure. In this paper, 3 nm FePt nanoparticles are first synthesized by superhydride re...
متن کاملSynthesis and Morphology of Face Centered Cubic (FCC) Fe-Pt Nanoparticles
FePt nanoparticles with thermally stable room-temperature ferromagnetism are investigated. The monodisperse nanoparticles are prepared by chemical synthesis and a salt-matrix annealing technique. Structural and magnetic characterizations confirm the phase transition from the disordered face-centered cubic structure. In this paper, 3 nm FePt nanoparticles are first synthesized by superhydride re...
متن کاملSynthesis and Characteristics of FePt Nanoparticle Films Under In Situ-Applied Magnetic Field
In situ external magnetic field was applied during the synthesis of FePt nanoparticles via a chemical solution method. FePt nanoparticle films were prepared on Si by a drop-coating method with and without a magnetic field. Annealing at 700 °C in reductive atmosphere was explored to obtain ferromagnetic FePt L10 phase. The effect of in situ-applied magnetic field on the structure, morphology, an...
متن کاملخواص مغناطیسی بلوری آلیاژ نانوذرات آهن- پلاتین (L10-FePt) در گذار فاز
High magneto- crystalline anisotropy (ku=7×106j/m3) of L10-FePt nanoparticles are an excellent candidate for ultra high-density magnetic recording. The 4 nm FePt nanocrystals were prepared by superhydride reduction of FeCl2·4H2O and Pt(acac)2 precursors in the phenyl ether by reduction of the 1, 2-hexadecanediol and LiBEt3H superhydride. The crystal and magnetic structures were studied by XRD a...
متن کاملOne-step synthesis of FePt nanoparticles with tunable size.
A one-step synthesis of FePt nanoparticles is reported. The size, composition, and shape of the particles are controlled by varying the synthetic parameters such as molar ratio of stabilizers to metal precursor, addition sequence of the stabilizers and metal precursors, heating rate, heating temperature, and heating duration. An assembly of large (6 nm or greater) FePt nanoparticles, especially...