Ultrasonic Characterization of Interfaces in Composite Bonds

نویسندگان

  • N. Wang
  • O. I. Lobkis
  • S. I. Rokhlin
  • J. H. Cantrell
چکیده

The inverse determination of imperfect interfaces from reflection spectra of normal and oblique incident ultrasonic waves in adhesive bonds of multidirectional composites is investigated. The oblique measurements are complicated by the highly dispersed nature of oblique wave spectra at frequencies above 3MHz. Different strategies for bond property reconstruction, including a modulation method, are discussed. The relation of measured interfacial spring density to the physico-chemical model of a composite interface described by polymer molecular bonds to emulate loss of molecular strength on an adhesive composite interface is discussed. This potentially relates the interfacial (adhesion) strength (number of bonds at the adhesive substrate interface) to the spring constant (stiffness) area density (flux), which is an ultrasonically measurable parameter.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Sonosynthesis and characterization of nano ZnO/Montmorillonite nano clay composite via Sol-Gel method

Nano ZnO/ montmorillonite composite were prepared by sol gel method under ultrasonic irradiation from directly mixing montmorillonite nano clay into Zinc gel. The Zn(CH3COO)2.2H2O and montmorillonite nano clay was used as precursor. The zinc acetate was dissolved in DI water and, NH3 (aq) solution was dropped into the zinc solution until pH 9 consequently the zinc gel was produced. The montmori...

متن کامل

Sonosynthesis and characterization of nano ZnO/Montmorillonite nano clay composite via Sol-Gel method

Nano ZnO/ montmorillonite composite were prepared by sol gel method under ultrasonic irradiation from directly mixing montmorillonite nano clay into Zinc gel. The Zn(CH3COO)2.2H2O and montmorillonite nano clay was used as precursor. The zinc acetate was dissolved in DI water and, NH3 (aq) solution was dropped into the zinc solution until pH 9 consequently the zinc gel was produced. The montmori...

متن کامل

Preparation and Characterization of ZrO2/ZnO Nanocomposite under Ultrasonic Irradiation via Sol-gel Route

Nanocomposite of ZrO2/ZnO was prepared under ultrasonic irradiation by sol gel process from directly mixing Zirconium and Zinc gels, and the mixture was placed under ultrasonic irradiation for 2 hours then aging time the filtrated composite gel was calcinated at 500°C for 3h in furnace. The precursor sol of zirconium was prepared from an aqueous solution of ZrCl4 and zinc acetate dihydrated was...

متن کامل

Preparation and Characterization of ZrO2/ZnO Nanocomposite under Ultrasonic Irradiation via Sol-gel Route

Nanocomposite of ZrO2/ZnO was prepared under ultrasonic irradiation by sol gel process from directly mixing Zirconium and Zinc gels, and the mixture was placed under ultrasonic irradiation for 2 hours then aging time the filtrated composite gel was calcinated at 500°C for 3h in furnace. The precursor sol of zirconium was prepared from an aqueous solution of ZrCl4 and zinc acetate dihydrated was...

متن کامل

Sonosynthesis and Characterization of TiO2/ZrO2 Nanocomposite and Photocatalytic degradation of Congo red Dye under UV Light

NanoTiO2 , nanoZrO2 and TiO2 /ZrO2 nanocomposite were prepared via sol gel method by using ultrasonic irradiation. The precursor sol of zirconium was prepared from an aqueous solution of ZrCl4 and titanium tetra 2-propoxide was diluted by 2-propanol and deionized water The TiO2 /ZrO2 nanocomposite was synthesized from directly mixing Titanium dried gel into Zirconium gel. The reaction mixture w...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2010