Plasma spray deposition of tri-layer environmental barrier coatings

n air plasma spray process has been used to deposit tri-layer environmental barrier coatings consisting of a silicon bond coat, a mullite interiffusion barrier, and a Yb2SiO5 top coat on SiC substrates. Solidified droplets in as-deposited Yb2SiO5 and mullite layers were discovered to be epleted in silicon. This led to the formation of an Yb2SiO5 + Yb2O3 two-phase top coat and 2:1 mullite (2Al2O3*SiO2) coat deposited from 3:2 ullite powder. The compositions were consistent with preferential silicon evaporation during transient plasma heating; a consequence of the high apor pressure of silicon species at plasma temperatures. Annealing at 1300 ◦C resulted in internal bond coat oxidation of pore and splat surfaces, recipitation of Yb2O3 in the top coat, and transformation of 2:1 mullite to 3:2 mullite + Al2O3. Mud-cracks were found in the Yb2SiO5 layer and n precipitated Al2O3 due to the thermal expansion mismatch between these coating phases and the substrate. 2014 Elsevier Ltd. All rights reserved.