Spatial relationships between polymers in Sitka spruce: Proton spin-diffusion studies

The spatial arrangement of polymers in Sitka spruce (Picea sitchensis) was investigated by NMR proton spindiffusion studies, supplemented by deuterium-exchange experiments monitored by FTIR spectroscopy. The FTIR spectra of earlywood sections after vapour-phase exchange with deuterium oxide showed that 43% of the hydroxyl groups were accessible to deuteration. This value is lower than predicted in the absence of aggregation of cellulose microfibrils into larger units, but greater than the predicted level of deuteration if 3.5-nm microfibrils surrounded by hemicellulose sheaths were aggregated into 4=4 arrays without space for deuterium oxide to penetrate between the microfibrils. The rate of proton spin diffusion between lignin and cellulose was consistent with the presence of microfibril arrays with approximately these dimensions and with lignin located outside them, in both earlywood and latewood. Proton spin-diffusion data for hemicelluloses were complicated by difficulties in assigning signals to glucomannans and xylans, but there was evidence for the spatial association of one group of hemicelluloses, including acetylated glucomannans, with cellulose surfaces, while another group of hemicelluloses was in spatial proximity to lignin. These data are consistent with a number of nanoscale models for the Sitka spruce cell wall, including a model in which glucomannans are associated with microfibril surfaces within the aggregate and water can penetrate partially between these surfaces, and one in which all non-cellulosic polymers and water are excluded from the interior of each microfibril aggregate.