Wettability of amorphous and nanocrystalline Fe78B13Si9 substrates by molten Sn and Bi
نویسندگان
چکیده
The wettability of amorphous and annealing-induced nanocrystalline Fe78B13Si9 ribbons by molten Sn and Bi at 600 K was measured using an improved sessile drop method. The results demonstrate that the structural relaxation and crystallization in the amorphous substrates do not substantially change the wettability with molten Bi because of their invariable physical interaction, but remarkably deteriorate the wettability and interfacial bonding with molten Sn as a result of changing a chemical interaction to a physical one for the atoms at the interface.
منابع مشابه
Development of Wettability Evaluation Technique Applying Contact Angle Measurement during Soldering
Sn-3.5Ag (1%Cu 1%Zn 5%Bi 5%In) Cu Au A new wettability evaluating system was developed by combining a contact angle measurement instrument, which optically and insitu measures the contact angle of molten solder, with a conventional wettability tester (meniscograph). Using this new evaluation system, a well-known experiential knowledge that the wettability for Sn-3.5Ag, a typical Pbfree solder, ...
متن کاملDevelopment of Wettability Evaluation Technique
A new wettability evaluating system was developed by combining a contact angle measurement instrument, which optically and insitu measures the contact angle of molten solder, with a conventional wettability tester (meniscograph). Using this new evaluation system, a well-known experiential knowledge that the wettability for Sn-3.5Ag, a typical Pbfree solder, is inferior to that for Sn-37Pb is qu...
متن کاملEffect of Heat Treatment Time on the Characteristics of Coating Formed on Nanocrystalline Finemet Foils
In the present research, amorphous Fe73.5Si13.5B9Nb3Cu1 Finemet foils, 21-26µm in thickness and 5mm in width, were prepared by Planar Flow Casting (PFC) process. Wound cores of amorphous Finemet foils were simultaneously annealed and heat treated at 540°C for 60, 120 and 240 minutes in steam and air flow to form oxide insulating coating layer on both surfaces of the foils. The structure of nano...
متن کاملEFFECTS OF TiO2 ADDITIVE ON ELECTROCHEMICAL HYDROGEN STORAGE PROPERTIES OF NANOCRYSTALLINE /AMORPHOUS Mg2Ni INTERMETALLIC ALLOY
Abstract: Mg2Ni alloy and Mg2Ni–x wt% TiO2 (x = 3, 5 and 10 wt %) composites are prepared by mechanical alloying. The produced alloy and composites are characterized as the particles with nanocrystalline/amorphous structure. The effects of TiO2 on hydrogen storage properties are investigated using anodic polarization and electrochemical impedance spectroscopy. It is demonstrated that the initia...
متن کاملبررسی سینتیک نانو تبلور نوارهای نرم مغناطیس FINEMET در شرایط غیرهمدما
The soft magnetic nanocrystalline Fe73.5Si13.5B9Cu1Nb3 alloy (FINEMET®) is produced by heat treatment of amorphous precursor. Determining kinetic parameters of amorphous structure transformation to nanocrystalline allows the control of microstructure (e.g. size and volume fraction of nanocrystalline grains) in order to achieve desired soft magnetic properties by optimizing the heat treatment co...
متن کامل