Utilization of Mineral Wools as Alkali-Activated Material Precursor
نویسندگان
چکیده
Mineral wools are the most common insulation materials in buildings worldwide. However, mineral wool waste is often considered unrecyclable because of its fibrous nature and low density. In this paper, rock wool (RW) and glass wool (GW) were studied as alkali-activated material precursors without any additional co-binders. Both mineral wools were pulverized by a vibratory disc mill in order to remove the fibrous nature of the material. The pulverized mineral wools were then alkali-activated with a sodium aluminate solution. Compressive strengths of up to 30.0 MPa and 48.7 MPa were measured for RW and GW, respectively, with high flexural strengths measured for both (20.1 MPa for RW and 13.2 MPa for GW). The resulting alkali-activated matrix was a composite-type in which partly-dissolved fibers were dispersed. In addition to the amorphous material, sodium aluminate silicate hydroxide hydrate and magnesium aluminum hydroxide carbonate phases were identified in the alkali-activated RW samples. The only crystalline phase in the GW samples was sodium aluminum silicate. The results of this study show that mineral wool is a very promising raw material for alkali activation.
منابع مشابه
Preparation and Properties of Alkali Activated Metakaolin-Based Geopolymer
The effective activation and utilization of metakaolin as an alkali activated geopolymer precursor and its use in concrete surface protection is of great interest. In this paper, the formula of alkali activated metakaolin-based geopolymers was studied using an orthogonal experimental design. It was found that the optimal geopolymer was prepared with metakaolin, sodium hydroxide, sodium silicate...
متن کاملEffect of Na3PO4 on the Hydration Process of Alkali-Activated Blast Furnace Slag
In recent years, the utilization of different non-traditional cements and composites has been increasing. Alkali-activated cementitious materials, especially those based on the alkali activation of blast furnace slag, have considerable potential for utilization in the building industry. However, alkali-slag cements exhibit very rapid setting times, which are too short in some circumstances, and...
متن کامل2. Relevance to Public Health 2.1 Background and Environmental Exposures to Synthetic Vitreous Fibers in the United States
Synthetic vitreous fibers are inorganic fibrous materials, manufactured principally from glass, rock, minerals, slag, and processed inorganic oxides. Synthetic vitreous fibers are manufactured by several processes, all of which involve cooling of a stream of high-temperature, molten inorganic oxides. Commercially important synthetic vitreous fibers are primarily silica-based, but contain variou...
متن کاملEnzymatic Hydrolysis of Olive Industry Solid Waste into Glucose, the Precursor of Bioethanol
Olive industry solid waste (OISW) is a by-product generated in the process of olive oil extraction. It is a lignocellulosic material consisting of cellulose, hemicelluloses, lignin and other extractives. In this work, a process for hydrolyzing the OISW into its monomers glucose, the precursor of bioethanol was developed. The hydrolysis process involves two stages: in the first stage, the O...
متن کامل