High Active Zn/Mg-Modified Ni–P/Al2O3 Catalysts Derived from ZnMgNiAl Layered Double Hydroxides for Hydrodesulfurization of Dibenzothiophene
نویسندگان
چکیده
A series of ZnMgNiAl layered double hydroxides (LDHs) containing 20 wt.% Ni and different Zn/Mg molar ratios were prepared by a coprecipitation method, and then were introduced with H2PO4 via a microwave-hydrothermal method. With the resulting mixtures as the precursors, Zn/Mg-modified ZnMgNi–P/Al2O3 catalysts were prepared. The Zn/Mg molar ratio affected the formation of Ni2P and Ni12P5 in nickel phosphides. The ZnMgNi–P/Al2O3 catalyst with a Zn/Mg molar ratio of 3:1 exhibits the best dibenzothiophene hydrodesulfurization (HDS) activity. Compared with the Ni–P/Al2O3 catalyst prepared from the impregnation method, the ZnMgNi–P/Al2O3 catalyst shows a higher HDS activity (81.6% vs. 54.3%) and promotes the direct desulfurization of dibenzothiophene.
منابع مشابه
Sonochemical preparation of supported hydrodesulfurization catalysts.
Sonochemical preparation of Co and Ni promoted MoS(2) supported on alumina was achieved by high-intensity ultrasonic irradiation of isodurene solutions containing molybdenum carbonyl, dicobalt octacarbonyl, elemental sulfur, and Al(2)O(3) or Ni-Al(2)O(3) under Ar flow. The sonochemically prepared catalysts were characterized by elemental analysis, XPS, SEM, TEM, and XEDS, and hydrodesulfurizati...
متن کاملLayered double hydroxides: Novel nanocatalysts for combustion of gaseous toluene from polluted air
The catalytic performance of Ni-Al, Mg-Al, and Co-Ni LDHs as novel nanocatalysts was evaluated in the oxidation of toluene. The samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), and Fourier transform infrared spectroscopy (FTIR). The XRD and FTIR approved the structure and functional groups of the LDH, respectively. Also, the presence of cations with dif...
متن کاملAdsorptive desulfurization of oil derivatives using nanostructured Mg-Al layered double hydroxides: Experimental design and modeling
This study focuses on the application of nanostructured Mg-Al layered double hydroxide as a promising adsorbent in desulfurization of dibenzothiophene, an aromatic sulfur bearing compound from gasoil model. The Mg-Al LDH was synthesized by a co-precipitation method and characterized by FT-IR, XRD, EDX and SEM. The XRD and FT-IR approved the layered structure and crystalline form of the adsorben...
متن کاملAdsorptive desulfurization of oil derivatives using nanostructured Mg-Al layered double hydroxides: Experimental design and modeling
This study focuses on the application of nanostructured Mg-Al layered double hydroxide as a promising adsorbent in desulfurization of dibenzothiophene, an aromatic sulfur bearing compound from gasoil model. The Mg-Al LDH was synthesized by a co-precipitation method and characterized by FT-IR, XRD, EDX and SEM. The XRD and FT-IR approved the layered structure and crystalline form of the adsorben...
متن کاملCompetitive sorption of Ni and Zn at the aluminum oxide/water interface: an XAFS study
Trace metals (e.g. Ni, Zn) leached from industrial and agricultural processes are often simultaneously present in contaminated soils and sediments. Their mobility, bioavailability, and ecotoxicity are affected by sorption and cosorption at mineral/solution interfaces. Cosorption of trace metals has been investigated at the macroscopic level, but there is not a clear understanding of the molecul...
متن کامل