Optimizing Strength Characteristics of Powder Workpieses of Fe-C-Cu System
نویسنده
چکیده
In this publication is presented optimization strength properties – tensile strength and elongation, of sintered structural materials of Fe-C-Cu system. Optimization is camed out by the method of simplex lattices adduced.Are presented grafphical relationships amending studied harakteristiks depending on the concentration of the elements in the triple system.
منابع مشابه
On the development of direct metal laser sintering for rapid tooling
An iron based powder blend has been developed for rapid tooling using a direct laser sintering process. The powder consists of a mixture of different elements including Fe, C, Cu, Mo and Ni. High sintering activities were obtained by tailoring the powder characteristics and optimizing the chemical constituents. The manufacturing of complex-shaped parts is possible at rates of 6.75 cm3/h accordi...
متن کاملStructure and Strength of Iron-Copper-Carbon Nanotube Nanocomposites
Nanocomposite materials of the Fe-Cu system with/without small addition of carbon nanotubes have been synthesized by mechanochemical activation of elemental Fe and Cu powders in a high-energy planetary ball mill and have been examined by the X-ray diffraction method, SEM and the thermopower methods; the tensile strength of the materials obtained has been estimated. The metastable (Fe, Cu) super...
متن کاملProduction of W-Cu-Ni Alloy and Cu Bimetal by SPS Process and Analysis of Process Parameters
This study aims at investigating changes in microstructure and strength of W alloy and Cu bimetals with varying spark plasma sintering (SPS) temperature and percentage of copper in W-Cu-Ni alloy. After SPS of W (12 wt%)-Cu (14 wt%)-Ni (3 wt%) alloy powder into consolidated discs at 1350 ° C, they were spark plasma sintered to copper discs at various temperatures. Assessment of the interface mic...
متن کاملOptimizing the Preparation Conditions of Silica Supported Fe-Co-Ce Ternary Catalyst for the Fixed-bed Fischer-Tropsch Synthesis: Taguchi Experimental Design Approach
Using wet impregnation method, a novel ternary system of silica supported Fe-Co-Ce catalyst was prepared. Preparation conditions such as impregnation time and temperature, drying time and temperature, were optimized by the L9 Taguchi experimental design to achieve a light olefin selective catalyst with maximum CO conversion in a fixed bed micro-reactor. It was found that the best conditions to ...
متن کاملStrong and Stable Nanocomposites Prepared by High-Pressure Torsion of Cu-Coated Fe Powders
Segregation and chemical inhomogeneity are well-known problems in powder metallurgy and are also an issue for new applications of powder mixtures, for example as starting materials for severe plastic deformation. In this study, Cu-coated Fe powder was prepared via immersion deposition, inductively hot-pressed and subsequently deformed using high-pressure torsion. The homogeneity of the pressed ...