Controlled growth of ordered nanopore arrays in GaN.
نویسندگان
چکیده
High-quality, ordered nanopores in semiconductors are attractive for numerous biological, electrical, and optical applications. Here, GaN nanorods with continuous pores running axially through their centers were grown by organometallic vapor phase epitaxy. The porous nanorods nucleate on an underlying (0001)-oriented GaN film through openings in a SiN(x) template that are milled by a focused ion beam, allowing direct placement of porous nanorods. Nanopores with diameters ranging from 20-155 nm were synthesized with crystalline sidewalls.
منابع مشابه
Ordered Nanoporous Alumina Membranes Formed in Oxalic/Phosphoric Acid Using Hard Anodization
Highly self-ordered alumina nanopore arrays were fabricated using hard anodization technique in different mixtures of oxalic/phosphoric acid. The phosphoric acid concentration was varied from 0.05 to 0.3 M while the oxalic acid concentration was changed between 0.3 and 0.4 M. The self ordered nanoporous arrays were obtained in anodization voltage changing from 130 to 200 V. The interpore distan...
متن کاملFabrication of ordered nanoporous anodic alumina prepatterned by mold-assisted chemical etching
In this article, a simple and cost-effective method to create patterned nanoindentations on Al surface via mold-assisted chemical etching process is demonstrated. This report shows the reaction-diffusion method which formed nanoscale shallow etch pits by the absorption/liberation behaviors of chemical etchant in poly(dimethylsiloxane) stamp. During subsequent anodization, it was possible to obt...
متن کاملInGaN/GaN multiple quantum wells grown on nonpolar facets of vertical GaN nanorod arrays.
Uniform GaN nanorod arrays are grown vertically by selective area growth on (left angle bracket 0001 right angle bracket) substrates. The GaN nanorods present six nonpolar {1⁻100} facets, which serve as growth surfaces for InGaN-based light-emitting diode quantum well active regions. Compared to growth on the polar {0001} plane, the piezoelectric fields in the multiple quantum wells (MQWs) can ...
متن کاملHighly ordered GaN-based nanowire arrays grown on patterned (100) silicon and their optical properties.
Arrays of GaN-based nanowires have been synthesized on patterned silicon without a catalyst. The spatial density, length and average radius of the nanowires can be well-controlled. The GaN core contains two semipolar facets and a controllable polar facet. The nanowire heterostructures exhibit excellent laser behavior.
متن کاملAluminum Nanowire Arrays via Directed Assembly.
Freestanding and vertically-oriented metal nanowire arrays have potential utility in a number of applications, but presently lack a route to fabrication. Template-based techniques, such as electrodeposition into lithographically defined nanopore arrays, have produced well-ordered nanowire arrays with a maximum pitch of about 2 μm; such nanowires, however, tend to cluster due to local attractive...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Nano letters
دوره 11 2 شماره
صفحات -
تاریخ انتشار 2011