Low-temperature synthesis of high-ordered anatase TiO2 nanotube array films coated with exposed {001} nanofacets
نویسندگان
چکیده
High-ordered anatase TiO2 nanotube array films coated with exposed high-reactive {001} nanofacets were fabricated by a modified hydrothermal method using amorphous anodic TiO2 nanotube arrays (ATONAs) as starting materials. It was found that the reaction between gas phase HF and solid ATONAs played a key role in the transformation process from amorphous to anatase TiO2, and the TiO2 tubular structure kept unchanged during the surface modification with an exposed {001} facets up to 76.5%, which could be attributed to the low reaction temperature of 130 °C. Our study provided a novel route for the facile preparation of {001} facets exposed anatase TiO2.
منابع مشابه
Synthesis and Characterization of Anatase-coated Multiwall Carbon Nanotube for Improvement of Photocatalytic Activity
Sol-gel technique was used to coat multiwall carbon nanotubes (MWCNTs) with anatase titania to increasing the surface area and improve the photocatalytic activity of TiO2. Room temperature ballistic conduct of MWCNT combined with semiconducting behavior of anatase brought about a photocatalytic improvement of ~37 % with respect to the highest methyl orange decolorization flair. For characteriza...
متن کاملEffect of annealing temperature on wettability of TiO2 nanotube array films
Highly ordered TiO2 nanotube array (TN) films were prepared by anodization of titanium foil in a mixed electrolyte solution of glycerin and NH4F and then annealed at 200°C, 400°C, 600°C, and 800°C, respectively. The samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), water contact angle (WCA), and photoluminescence (PL). It was found that low temperature (...
متن کاملAnatase TiO2 nanotube powder film with high crystallinity for enhanced photocatalytic performance
We report on the synthesis of TiO2 nanotube (NT) powders using anodic oxidation and ultrasonication. Compared to free-standing NT array films, the powder-type NTs can be easily fabricated in a cost-effective way. Particularly, without the substrate effect arising from underlying Ti metals, highly crystallized NT powders with intact tube structures and pure anatase phase can be obtained using hi...
متن کاملSTUDY OF ANNEALING TEMPERATURE VARIATION ON THE STRUCTURAL PROPERTIES OF DIP-COATED TiO2-SiO2 NANOSTRUCTURED FILMS
Abstract:In the present research, SiO2–TiO2 nanostructure films were successfully prepared on windshields using the sol–gel technique for photocatalytic applications. To prevent the thermal diffusion of the sodium ions from the glass to TiO2 films, the SiO2 layer was pre-coated on the glass by the sol–gel method. The substrates were dipped in the sol and withdrawn with the speed of 6cm/min-1 to...
متن کاملOn the Investigation of Sol-Gel TiO2 Nanostructured Films Applied on Windshields Pre-Coated with SiO2 Layer by Dip-Coating Method
TiO2-SiO2 photocatalytic nanostructure film on windshield for self-cleaning purposes was prepared via sol–gel dip-coating method. TiO2 films were prepared on automotive glass pre-coated with a SiO2 layer by a dip-coating method followed by annealing at 500 °C for 30min. The films were characterized using X-ray diffraction XRD and scanning electron microscopy SEM, FE-SEM techniques. The TiO2-SiO...
متن کامل