High-temperature behaviour of average structure and vibrational density of states in the ternary superionic compound AgCuSe

Results of simultaneous thermal analysis (STA), synchrotron powder diffraction (in the range 300–973 K) and inelastic neutron scattering (at 285 and 505 K) on non-superionic βand superionic α-AgCuSe are reported. The sample is stable in argon on heating. The volume change at the superionic phase transition is about 5%. A model for the average structure of α-AgCuSe is proposed. No anomalies in the temperature dependence of the parameters of the average structure were revealed. Ionic conductivity in α-AgCuSe can originate from cation jumps in “skewed” 〈100〉 directions between nearest-neighbour tetrahedral sites via the peripheries of the octahedral cavities. A correlation between the temperature dependence of the cation redistribution in α-AgCuSe and the temperature dependence of the ionic conductivity is supposed. Various contributions (anharmonic effects, time-average static disorder and phononphonon scattering) to the widths of individual phonons upon temperature increase lead to pronounced changes in the neutron-weighted densities of states of βand α-AgCuSe and accompany the superionic phase transition as well. PACS. 61.43.-j Disordered solids – 61.10.-i X-ray diffraction and scattering – 78.70.Nx Neutron inelastic