Enhancement of Critical Current across Single Grain Boundaries in YBa2Cu3Ox and Search for Superconductivity in Alkali Metals
نویسنده
چکیده
The ability of single grain boundaries in YBa2Cu3Ox bicrystalline rings to carry electrical current is found to be significantly enhanced under hydrostatic pressure. Nearly hydrostatic pressures are applied to the alkali metals Li, Na, and K. in a search for superconductivity. Whereas Li becomes superconducting above 20 GPa at temperatures as high as 15 K, no superconductivity was observed above 4 K in Na to 65 GPa nor in K above 4 K to 43.5 GPa or above 1.5 K to 35 GPa.
منابع مشابه
Enhanced superconducting properties of bicrystalline YBa2Cu3Ox and alkali metals under pressure
Nearly hydrostatic pressures are found to enhance the critical current density Jc through single grain boundaries in YBa2Cu3Ox rings and to induce superconductivity in Li. Whereas Li becomes superconducting above 20 GPa at temperatures as high as 15 K, no superconductivity was observed above 4 K in Na to 65 GPa nor in K above 4 K to 43.5 GPa or above 1.5 K to 35 GPa.
متن کاملEnhancement of the critical current density of YBa2Cu3Ox superconductors under hydrostatic pressure.
The dependence of the critical current density Jc on hydrostatic pressure to 0.6 GPa is determined for a single 25 degrees [001]-tilt grain boundary in a bicrystalline ring of nearly optimally doped melt-textured YBa2Cu3Ox. Jc is found to increase rapidly under pressure at +20%/GPa. A new diagnostic method is introduced (pressure-induced Jc relaxation) which reveals a sizable concentration of v...
متن کاملPressure-induced enhancement of the critical current density in superconducting YBa2Cu3Ox bicrystalline rings
The dependence of the critical current density Jc T on hydrostatic He-gas pressure to 0.6 GPa is determined for nearly optimally doped and strongly underdoped melt-textured YBa2Cu3Ox bicrystalline rings containing single 001 -tilt grain boundaries GBs with mismatch angles from 0° to 31°. For all samples with 0°, Jc is found to increase rapidly under pressure, the rate of increase lying predomin...
متن کاملQuenching Effect on the Pb-Substituted Bi-Based Bulk Ceramic Superconductors
The effect of cooling process for the synthesis and the superconductivity properties of Pb-substituted Bi-based materials, has been investigated. The preparation condition for the formation of (2,2,2,3) phase has been examined. The influence of thermal condition of the synthesis and quenching on the critical temperature and the content of 110K phase was investigated. Results of the ac-susceptib...
متن کاملSelf-generated magnetic flux in YBa2Cu3O7Àx grain boundaries
Grain boundaries in high-Tc cuprates are interesting and important for both fundamental physics and applications of high-temperature superconductivity. Conventional models of strongly coupled Josephson junctions are applicable to describe electromagnetic properties of grain boundaries in thin films of high-Tc superconductors. 4,5 A remarkable exception of this rule is the @001#-tilt boundary in...