Time and energy resolved ion mass spectroscopy studies of the ion flux during high power pulsed magnetron sputtering of Cr in Ar and Ar/N2 atmospheres
نویسندگان
چکیده
Mass spectroscopy was used to analyze the energy and composition of the ion flux during high power pulsed magnetron sputtering (HIPIMS/HPPMS) of a Cr target in an industrial deposition system. The ion energy distribution functions were recorded in the time-averaged and time-resolved mode for Ar + , Ar 2+ , Cr + , Cr 2+ , N2 + and N + ions. In the metallic mode the dependence on pulse energy (equivalent of peak target current) was studied. In the case of reactive sputtering in an Ar/N2 atmosphere, variations in ion flux composition were investigated for varying N2-to-Ar flow ratio at constant pressure and HIPIMS power settings. The number of doubly charged Cr ions is found to increase linearly with increasing pulse energy. An intense flux of energetic N + ions was observed during deposition in the reactive mode. The time evolution of ion flux composition is analyzed in detail and related to the film growth process. The ionization of working gas mixture is hampered during the most energetic phase of discharge by a high flux of sputter-ejected species entering the plasma, causing both gas rarefaction and quenching of the electron energy distribution function. It is suggested that the properties (composition and energy) of the ion flux incident on the substrate can be intentionally adjusted not only by varying the pulse energy (discharge peak current), but also by taking advantage of the observed time-variations in the composition of ion flux. keywords: high power pulsed magnetron sputtering; HPPMS; high power impulse magnetron sputtering; HIPIMS; ion mass spectroscopy; ion energy distribution; plasma diagnostics; ion flux
منابع مشابه
CrNx Films Prepared by DC Magnetron Sputtering and High-Power Pulsed Magnetron Sputtering: A Comparative Study
CrNx (0 ≤ x ≤ 0.91) films synthesized using highpower pulsed magnetron sputtering, also known as high-power impulse magnetron sputtering (HiPIMS), have been compared with those made by conventional direct-current (dc) magnetron sputtering (DCMS) operated at the same average power. The HiPIMS deposition rate relative to the DCMS rate was found to decrease linearly with increasing emission streng...
متن کاملMicrostructure control of CrNx films during high power impulse magnetron sputtering
The microstructure and composition of CrNx ( 1 0 x ) films grown by reactive High Power Pulsed Magnetron Sputtering (HIPIMS or HPPMS) have been studied as a function of the process parameters: N2-to-Ar discharge gas ratio, (fN2/Ar), negative substrate bias (Vs), pulsing frequency, and energy per pulse. The film stoichiometry is found to be determined by the composition of the material flux inci...
متن کاملSilicon Nitride Based Coatings Grown by Reactive Magnetron Sputtering
Silicon nitride and silicon nitride-based ceramics have several favorable material properties, such as high hardness and good wear resistance, which makes them important materials for the coating industry. This thesis focuses the synthesis of silicon nitride, silicon oxynitride, and silicon carbonitride thin films by reactive magnetron sputtering. The films were characterized based on their che...
متن کاملGas rarefaction effects during high power pulsed magnetron sputtering of groups IVb and VIb transition metals in Ar
We use energyand time-dependent mass spectrometry to analyze the evolution of metaland gas-ion fluxes incident at the substrate during high-power pulsed magnetron sputtering (HiPIMS) of Groups IVb and VIb transition-metal (TM) targets in Ar. For all TMs, the time-and energy-integrated metal/gas-ion ratio at the substrate plane NNMMMM+/NNAAAA+ increases with increasing peak target current densit...
متن کامل