Inhibition of Pipelines Corrosion Using Natural Extracts
نویسنده
چکیده
The present work is aimed at examining carbon steel oil pipelines corrosion using three natural extracts (Eruca Sativa, Rosell and Mango peels) that are used as inhibitors of different concentrations ranging from 0.05-0.1wt. %. Two sulphur compounds are used as corrosion mediums. Weight loss method was used for measuring the corrosion rate of the carbon steel specimens immersed in technical white oil at 100oC at various time intervals in absence and presence of the two sulphur compounds. The corroded specimens are examined using the chemical wear test, scratch test and hardness test. The scratch test is carried out using scratch loads from 0.5 Kg to 2.0 Kg. The scratch width is obtained at various scratch load and test conditions. The Brinell hardness test is carried out and investigated for both corroded and inhibited specimens. The results showed that three natural extracts can be used as environmentally friendly corrosion inhibitors. Keywords—Inhibition, natural extract, pipelines corrosion, sulphur compounds.
منابع مشابه
Effect of Structural Changes on Corrosion Inhibition Behavior of Synthesized N2O4 Imine Compounds for Steel Pipelines in Oil and Gas Wells
The inhibition properties of synthesized imine compounds N,Nʹ-bis(2,4-dihydroxyhydroxybenzaldehyde)-1,3-Propandiimine, N, N′-bis(2,4-dihydroxypropiophenone)-2,2-dimethylpropandiimine, N,Nʹ-bis(2,4-dihydroxyacetophenone)-1,3-Propandiimine has been investigated for API-5L-X65 steel corrosion in hydrochloric acid by scanning electron microscopy, potentiodynamic polarization and impedance spectrosc...
متن کاملEffect of Aaronsohnia Pubescens Extracts to Prevent Against the Corrosion of Mild Steel in 1.0 M HCl
The corrosion inhibition and adsorption (CIA) performance of the aqueous extracts of Aaronsohnia pubescens aerial parts (Odorized aqueous extract (OE) and Deodorized aqueous extract (DE)) on the corrosion mild steel (MS) in 1M hydrochloric acid were evaluated. It is based on the weight loss (WL) analysis, kinetic and thermodynamic parameters, and electrochemical methods both stationary (Potenti...
متن کاملAqueous Extracts of Santolina Pectinata lag., Aerial Parts as Green Corrosion Inhibitor for Mild Steel in 1.0 M HCl
The protective effect of the aqueous extracts of Santolina pectinata (Lag.) aerial parts (Odorized aqueous extract (AE1) and Deodorized aqueous extract (AE2)) on the corrosion of mild steel (MS) in 1M HCl solution were tested by the weight loss (WL) analysis, potentiodynamic polarization (PDP) and electrochemical impedance spectroscopy (EIS) methods. The inhibition efficiency (%IE) is highly ra...
متن کاملGreen Corrosion Inhibitor for Carbon Steel by Marrubium astranicum Leaves Extracts in 1 M HCl
The aim of this study was to investigate the effect of inhibition of Marrubium astranicumleaves extract on the corrosion of carbon steel in hydrochloric acid solution by using weightloss and tafel polarization methods. Inhibition was found to increase with increasingconcentration of the leaves extract. The inhibition efficiency of this extract at an optimumconcentration of 100 mg L-1 was 99.9 %...
متن کاملTalinum triangulare leaf and Musa sapientum peel extracts as corrosion inhibitors on ZA-27 Alloy
With the current emergence of green chemistry to keep the environment safe, attention is being shifted towards using plant extracts as corrosion inhibitors. The inhibitive performances of Talinum triangulare leaf extract and Musa sapientum peel extract on the ZA-27 in 1.0 M and 1.5 M hydrochloric acid solutions were studied for 18 days using mass loss measurement. The corrosion inhibition effic...
متن کامل