Influence of Solution Properties and Process Parameters on the Formation and Morphology of YSZ and NiO Ceramic Nanofibers by Electrospinning
نویسندگان
چکیده
The fabrication process of ceramic yttria-stabilized zirconia (YSZ) and nickel oxide nanofibers by electrospinning is reported. The preparation of hollow YSZ nanofibers and aligned nanofiber arrays is also demonstrated. The influence of the process parameters of the electrospinning process, the physicochemical properties of the spinning solutions, and the thermal treatment procedure on spinnability and final microstructure of the ceramic fibers was determined. The fiber diameter can be varied from hundreds of nanometers to more than a micrometer by controlling the solution properties of the electrospinning process, while the grain size and surface roughness of the resulting fibers are mainly controlled via the final thermal annealing process. Although most observed phenomena are in qualitative agreement with previous studies on the electrospinning of polymeric nanofibers, one of the main differences is the high ionic strength of ceramic precursor solutions, which may hamper the spinnability. A strategy to control the effective ionic strength of precursor solutions is also presented.
منابع مشابه
Chitosan/nanosilver Nanofiber Composites with Enhanced Morphology and Microbiological Properties
In recent years natural polymers have been widely used in biomedical applications. Application of natural and biocompatible polymers in wound dressing, medical sutures and tissue engineering are extensively growing. Additional properties are provided when metal nanoparticles such as silver and gold are incorporated in to the fibers. However, nowadays nanofibers due to their inherent properties ...
متن کاملElectrospinning Nanofibers Gelatin scaffolds: Nanoanalysis of properties and optimizing the process for tissue engineering functional
Electrospinning has been recognized as an efficient technique for the fabrication of polymernanofibers. Recently, various polymers have successfully been electrospun into ultrafine fibers.Electrospinning is an extremely promising method for the preparation of tissue engineering scaffolds.In this study, nanofibers gelatin was electrospun at 20% v/v optimized content. To produce...
متن کاملFormation of Poly(vinylidene fluoride) Nanofibers Part II: the elaboration of incompatibility in the electrospinning of its solutions
Poly(vinylidene fluoride) (PVDF) fibers with two molecular weights were prepared via electrospinning process. In this process, the concentration of spinning depended drastically on the gelation process. Also, it was experimentally smaller than obtained concentration in the solution entanglement number approach (SENA). Proof of this incompatibility was explained by the properties of PVDF a...
متن کاملFormation of Poly(vinylidenefluoride) Nanofibers: Part I Optimization by Using of Central Composite Design
Poly(vinylidene fluoride) (PVDF) nanofibers were prepared via electrospinning process. Several different factors influence on this process and application of experimental design for its optimization is of great importance. The central composite design (CCD) was used for planning and optimizing of the experiments and also, the analysis of variance (ANOVA) was employed for the statistical va...
متن کاملThe Effect of Adding Alginate Natural Polymer on the Structure of Polyvinyl Alcohol Biocompatible Nanofibers in Electrospinning Process
Background: Nowadays, in order to preserve the environment and sustainable development, the use of natural and renewable resources is a priority for industries. High performance and specific structure of nano-biocompatible materials has attracted researchers. In this research, alginate polymer, which is generally obtained from marine sources such as algae, was added to polyvinyl alcohol nanofi...
متن کامل