{225}γ habit planes in martensitic steels: from the PTMC to a continuous model
نویسندگان
چکیده
Fine twinned microstructures with {225}γ habit planes are commonly observed in martensitic steels. The present study shows that an equibalanced combination of twin-related variants associated to the Kurdjumov-Sachs orientation relationship is equivalent to the Bowles and Mackenzie's version of the PTMC for this specific {225}γ case. The distortion associated to the Kurdjumov-Sachs orientation relationship results from a continuous modeling of the FCC-BCC transformation. Thus, for the first time, an atomic path can be associated to the PTMC.
منابع مشابه
Transient liquid phase bonding of AISI 304L stainless steels with the austenitic and martensitic microstructures
In the present study, the effect of time and base metal microstructure on the Transient Liquid Phase (TLP) bonding of 304L stainless steel was studied. TLP was performed at 1050 0C for 5 and 60 minutes on the coarse grain austenitic and martensitic microstructure using BNi-2 interlayer. To prepare martensitic microstructure, as-received 304L was rolled at -15 0C up to 80% rolling reduction. TEM...
متن کاملTransient liquid phase bonding of AISI 304L stainless steels with the austenitic and martensitic microstructures
In the present study, the effect of time and base metal microstructure on the Transient Liquid Phase (TLP) bonding of 304L stainless steel was studied. TLP was performed at 1050 0C for 5 and 60 minutes on the coarse grain austenitic and martensitic microstructure using BNi-2 interlayer. To prepare martensitic microstructure, as-received 304L was rolled at -15 0C up to 80% rolling reduction. TEM...
متن کاملVariant selection in surface martensite
A significant variant selection is reported in isothermal martensite formed on the surface of an Fe-30% Ni sample. The selection phenomenon is modelled using different descriptions of the martensitic phase transformation. In particular, matrices based on the phenomenological theory of martensite crystallography, the Jaswon and Wheeler distortion, and the continuous face centred cubic-body centr...
متن کاملMicrostructure and Mechanical Properties of Cold Rolled AISI 304L and 316L Austenitic Stainless Steels during Reversion Annealing
Microstructural evolutions during annealing of cold rolled AISI 304L and AISI 316L stainless steels were studied. Cold rolled AISI 304L alloy was fully martensitic but cold rolled AISI 316L alloy was partially martensitic due to the higher stability of the austenite phase in the latter. During continuous heating to elevated temperatures, the complete reversion of strain-induced martensite at 75...
متن کاملA Corrosion Study of Grain-Refined 304L Stainless Steels Produced by the Martensitic Process
AISI 304L austenitic stainless steel with different grain sizes of 0.5 -12 μm was obtained through the martensitic process. Corrosion behavior of different samples was investigated in a 0.5M HCl solution using open circuit potential, potentiodynamic polarization and electrochemical impedance spectroscopy tests. Also, the correlation between the grain size and pitting corrosion resistance was as...
متن کامل