Evaluation of an Alkaline Fuel Cell for Multi- Fuel System

The performance of an alkaline fuel cell is investigated using three different fuels, e g., methanol, ethanol and sodium borohydride. Pt/C/Ni was used as anode whereas Mn/C/Ni was used as standard (Electro-Chem-Technic, UK) cathode for all the fuels. Thus, the alkaline fuel cell is used for multi-fuel system. Fresh mixture of electrolyte, potassium hydroxide (5M), and fuel (2M) was fed to and withdrawn from the AFC at a rate of 1 ml/min. The anode was prepared by dispersing platinum and activated carbon in Nafion (DuPont USA) dispersion and placing it onto a carbon paper (Lydall, USA). Finally prepared anode sheet was pressed onto Ni mesh and sintered to produce the required anode. The maximum power density of 16.5 mW/cm is obtained at 28 mA/cm of current density for sodium borohydride at 25 C. Whereas, methanol produces 31.5 mW/cm of maximum power density at 44 mA/cm of current density at 60 C.