Improved Hemolytic Performance of Blood Pump with Fluorine-Doped Hydrogenated Amorphous Carbon Coating
نویسندگان
چکیده
Fluorine-doped hydrogenated amorphous carbon (a-C:H:F) film was deposited on a flow-straightener, impeller and diffuser surface (SUS 304) of an enclosed-impeller type flow blood pump using the ionization deposition method with a source gas of C6F5H. The surface characteristics of the a-C:H:F film were examined using atomic force microscopy, X-ray photoelectron spectroscopy, and measurements of surface roughness, friction and surface potential. The a-C:H:F film tends to increase surface roughness and the negative surface charge. In addition, the surface energy and friction decrease with fluorine dopant in the a-C:H film. To estimate the hemolytic performance of a blood pump with the a-C:H:F film coating, the amount of hemolysis was measured using a mock circulatory system (in vitro test) with 500 mL of pig blood containing sodium citrate. In vitro test was conducted for 180 min with the blood flow and pump head maintained at 5 L/min and 100 mmHg, respectively. The a-C:H:F film coating reduced the amount of hemolysis and improved the hemolytic performance. Decreasing the surface energy and negative surface charge of the a-C:H:F film contributes to the improvement of the hemolytic performance. The a-C:H:F film coating is thus expected to be utilized in medical technology as a surface coating technology for artificial heart blood pumps.
منابع مشابه
Interface modification effect between p-type a-SiC:H and ZnO:Al in p-i-n amorphous silicon solar cells
Aluminum-doped zinc oxide (ZnO:Al) [AZO] is a good candidate to be used as a transparent conducting oxide [TCO]. For solar cells having a hydrogenated amorphous silicon carbide [a-SiC:H] or hydrogenated amorphous silicon [a-Si:H] window layer, the use of the AZO as TCO results in a deterioration of fill factor [FF], so fluorine-doped tin oxide (Sn02:F) [FTO] is usually preferred as a TCO. In th...
متن کاملMo-pecvd (metal-organic Plasma Enhanced Chemical Vapour Deposition) of Erbium-doped Hydrogenated and Deuterated Amorphous Carbon
Erbium (Er) ion has been widely used in silica fiber-based active photonic devices, given its characteristic emission around 1.5 μm. Hydrogenated and deuterated amorphous carbon (a-C:H and a-C:D, respectively), thin film materials offering tailorable opto-electronic properties, have not been explored thoroughly as host materials for Er. The objective of this research is to study the potential s...
متن کاملThe Effect of thickness parameter and Fluorine Dopant on Photocatalytic performance of TiO2 thin films
In this study, Pure and doped titania sols with Fluorine (F/Ti:0.06) dopant, were prepared by sol-gel method and Ammonium Fluoride(NH4F) as the precursor. They were deposited on glass substrates (soda lime) in a certain(optimum) nanometric thickness by the dip coating method. Coated samples were dried and calcined under the specific rate. Phase composition and optical properties of coatings wer...
متن کاملTelecom to mid-infrared spanning supercontinuum generation in hydrogenated amorphous silicon waveguides using a Thulium doped fiber laser pump source.
A 1,000 nm wide supercontinuum, spanning from 1470 nm in the telecom band to 2470 nm in the mid-infrared is demonstrated in a 800 nm x 220 nm 1 cm long hydrogenated amorphous silicon strip waveguide. The pump source was a picosecond Thulium doped fiber laser centered at 1950 nm. The real part of the nonlinear parameter of this waveguide at 1950 nm is measured to be 100 ± 10 W -1m-1, while the i...
متن کاملPreparation of fluorine-doped, carbon-encapsulated hollow Fe3O4 spheres as an efficient anode material for Li-ion batteries.
Herein we report the design and synthesis of fluorine-doped, carbon-encapsulated hollow Fe3O4 spheres (h-Fe3O4@C/F) through mild heating of polyvinylidene fluoride (PVDF)-coated hollow Fe3O4 spheres. The spheres exhibit enhanced cyclic and rate performances. The as-prepared h-Fe3O4@C/F shows significantly improved electrochemical performance, with high reversible capacities of over 930 mA h g(-...
متن کامل