Iodine Transfer Copolymerization of Vinylidene Fluoride and a-Trifluoromethacrylic Acid in Emulsion Process Without Any Surfactants
نویسندگان
چکیده
The synthesis of poly(VDF-co-TFMA) copolymers (where VDF and TFMA stand for vinylidene fluoride and α-trifluoromethacrylic acid, respectively) by iodine transfer polymerization without any surfactant is presented. First, the synthesis and the control of the copolymerization of VDF and TFMA were investigated in the presence of two chain transfer agents, 1-perfluorohexhyl iodide (C
منابع مشابه
Iodine Transfer Copolymerization of Vinylidene Fluoride and α - Trifluoromethacrylic acid in Emulsion process without any surfactants
The synthesis of poly(VDF-co-TFMA) copolymers (where VDF and TFMA stand for vinylidene fluoride and α-trifluoromethacrylic acid, respectively) by iodine transfer polymerization without any surfactant is presented. First, the synthesis and the control of the copolymerization of VDF and TFMA were investigated in the presence of two chain transfer agents, 1-perfluorohexhyl iodide (C
متن کاملSynthesis and Copolymerization of Fluorinated Monomers Bearing a Reactive Lateral Group. XX. Copolymerization of Vinylidene Fluoride with 4-Bromo-1,1,2-trifluorobut-1-ene
The radical copolymerization of vinylidene fluoride (VDF) with 4-bromo-1,1,2-trifluorobut-
متن کاملCopolymerization of vinylidene fluoride with 4-bromo-1,1,2-trifluoroethylene
The radical copolymerization of vinylidene fluoride (VDF) with 4-bromo-1,1,2-trifluorobut-
متن کاملFormation of Poly(vinylidene fluoride) Nanofibers Part II: the elaboration of incompatibility in the electrospinning of its solutions
Poly(vinylidene fluoride) (PVDF) fibers with two molecular weights were prepared via electrospinning process. In this process, the concentration of spinning depended drastically on the gelation process. Also, it was experimentally smaller than obtained concentration in the solution entanglement number approach (SENA). Proof of this incompatibility was explained by the properties of PVDF a...
متن کاملPerformance of Chemically Modified TiO2-poly (vinylidene fluoride) DCMD for Nutrient Isolation and Its Antifouling Properties
The surface properties of TiO2-PVDF nanocomposite membranes were investigated by incorporating different chemically modified TiO2 nanoparticles into the poly (vinylidene fluoride) (PVDF) matrix. The nanocomposite membranes were prepared via dual coagulation bath diffusion and the induced phase inversion method. The membrane surface morphologies were investigated by using SEM and AFM and related...
متن کامل