Effects of grain refinement and strength on friction and damage evolution under repeated sliding contact in nanostructured metals

نویسندگان

  • T. Hanlon
  • A. H. Chokshi
  • M. Manoharan
  • S. Suresh
چکیده

The early stage sliding contact fatigue behavior of nanocrystalline materials, with average and total range of grain sizes well below 100 nm, was studied. The evolution of friction and damage during repeated sliding contact in the nanocrystalline metals and alloys was systematically compared and contrasted with that in ultrafine-crystalline and microcrystalline materials so as to develop a broad perspective on the effects of grain size on sliding contact fatigue. Some critical experiments were performed to separate the effects of material strength and grain size on friction and damage evolution. Over the range of materials examined, strength rather than grain size appeared to dominate the steady-state friction coefficient and damage accumulation, each diminishing with substantial increases in material strength. q 2005 Elsevier Ltd. All rights reserved.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Deformation, structural changes and damage evolution in nanotwinned copper under repeated frictional contact sliding

Nanotwinned metals have the potential for use as structural materials by virtue of having a combination of high strength as well as reasonable ductility and damage tolerance. In the current study, the tribological response of nanotwinned copper has been characterized under conditions of repeated frictional sliding contact with a conical tip diamond indenter. Pure ultrafine-grained copper specim...

متن کامل

Effects of mechanical properties and surface friction on elasto-plastic sliding contact

Indentation hardness has been used extensively for material characterization and many recent computational studies have established quantitative relationships between elasto-plastic mechanical properties and the response in instrumented indentation. In contrast, very few studies have systematically quantified the effect of the plastic deformation characteristics on the frictional sliding respon...

متن کامل

Microstructural evolution of 304 austenitic stainless steel in friction stir welding process

Friction stir welding (FSW) was conducted on AISI 304 austenitic stainless steel plate with 2 mm thickness. The FSW was performed at a welding and rotational speeds of 50 mm/min and 400 rpm, respectively. Microstructure observations by the optical microscopy showed that a severe grain refinement occurred in the stir zone (SZ). Electron backscattered diffraction analysis (EBSD) results indicated...

متن کامل

Microstructural evolution of 304 austenitic stainless steel in friction stir welding process

Friction stir welding (FSW) was conducted on AISI 304 austenitic stainless steel plate with 2 mm thickness. The FSW was performed at a welding and rotational speeds of 50 mm/min and 400 rpm, respectively. Microstructure observations by the optical microscopy showed that a severe grain refinement occurred in the stir zone (SZ). Electron backscattered diffraction analysis (EBSD) results indicated...

متن کامل

Mechanical Behavior of an Ultrafine/Nano Grained Magnesium Alloy

The application of magnesium alloys is greatly limited because of their relatively low strength and ductility. An effective way to improve the mechanical properties of magnesium alloy is to refine the grains. As the race for better materials performance is never ending, attempts to develop viable techniques for microstructure refinement continue. Further refining of grain size requires, however...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2005