BET specific surface area and pore structure of MOFs determined by hydrogen adsorption at 20 K.
نویسندگان
چکیده
Low-pressure high-resolution hydrogen adsorption for the metal-organic framework MIL-101 are measured at 19.5 K and pressures below 57 kPa. The BET specific surface area and micropore volume are determined and compared to results from nitrogen adsorption at 77 K. Steps in the hydrogen adsorption isotherm are correlated to the pore structure of MIL-101.
منابع مشابه
Hydrogen adsorption by g-C3N4 and graphene oxide nanosheets
The adsorption behavior of hydrogen for synthesized graphitic carbon nitride (g-C3N4) and graphene oxide nanosheets was compared. The structure of the prepared g-C3N4 and graphene oxide samples were studied using TEM, FT-IR spectroscopy and surface area analysis. Textural results of the prepared nanosheets show that the surface area, total pore volume, and average internal diameter of g-C3N4 an...
متن کاملSynthesis and Characterization of Zn3 (BTC)2 Nanoporous Sorbent and its Application for Hydrogen Storage at Ambient Temperature
Metal organic frameworks (MOFs) are considered an interesting option for hydrogen storage. These materials show an exceptional H2 uptake. Here, Zn3(BTC)2 as MOF was synthesized with a solvothermal method. The phase stability and microstructure of the Zn3(BTC)2 was characterized in terms of their properties and structures, using a number of analytical techniques including FT-IR, XRD, SEM, BET ...
متن کاملبررسی قابلیت جذب هیدروژن در ماده مرکب نانو‌ساختار SBA-16-Pd
The purpose of this work was to study the hydrogen adsorption on the surface of mesoporous materials based on silica (SBA-16) modified with palladium via temperature. Since mesoporous silica materials have a high specific surface area, and the ordered mesoporous size of 2-10nm, they are suitable for adsorption and storage of hydrogen. SBA-16 is suitable for this purpose due to its cubic crystal...
متن کاملPd Nanoparticles and MOFs Synergistically Hybridized Halloysite Nanotubes for Hydrogen Storage
Natural halloysite nanotubes (HNTs) were hybridized with metal-organic frameworks (MOFs) to prepare novel composites. MOFs were transformed into carbon by carbonization calcination, and palladium (Pd) nanoparticles were introduced to build an emerging ternary compound system for hydrogen adsorption. The hydrogen adsorption capacities of HNT-MOF composites were 0.23 and 0.24 wt%, while those of ...
متن کاملInvestigation of hydrogen sulfide adsorption in metallic scaffold MOF-5 nanocomposite based on activated carbon for the use of respiratory mask cartridge
Introduction: Hydrogen sulfide is one of the most important impurities in natural gas. Due to the fact that this gas is hazardous, toxic, corrosive and volatile, therefore, the removal of hydrogen sulfide has been studied using several methods. One of the most known procedures is the adsorption process. In the present study, activated carbon and activated carbon-based composite scaffolds (MOF-5...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Physical chemistry chemical physics : PCCP
دوره 13 8 شماره
صفحات -
تاریخ انتشار 2011