DC bias immune nanocrystalline magnetic cores made of Fe73Nb3Cu1B7Si16 ribbon with induced transverse magnetic anisotropy
نویسندگان
چکیده
The comparative analysis of magnetic properties of cut cores made of nanocrystalline Fe73Nb3Cu1B7Si16 alloy ribbon and cores made of the same ribbon with preliminary tension-induced transverse magnetic anisotropy was carried out. The possibility of improving magnetic properties of cut cores, decreasing loss, and increasing DC bias immunity of reversible magnetic permeability is presented. The influence of induced magnetic anisotropy on DC bias immunity of reversible magnetic permeability was investigated. The advantages and disadvantages of new cores (made of ribbon heated under tensile stress) over cut ones were determined.
منابع مشابه
Soft magnetic properties of nanocrystalline Fe73B7Si16Nb3Cu1 alloy after rapid heating under tensile stress
Amorphous Fe73B7Si16Nb3Cu1 ribbon was crystallized rapidly by electric current heating under simultaneously applied tensile stress along the ribbon axis. As a result, strong transverse magnetic anisotropy was induced in the ribbon. Dynamic magnetic properties of the ribbons rapidly heated either under the tensile stress or without tensile stress were measured using toroidal cores. Optimal elect...
متن کاملEffect of Mechanical Stresses in Rapidly Heated Fe73Cu1Nb3Si16B7 Ribbon Arising During the Ring Core Formation on Their Magnetic Properties
The influence of winding-induced mechanical stresses on the magnetic anisotropy and core loss in toroidal cores made of Fe73Cu1Nb3Si16B7 ribbon is studied. The ribbon for the cores was rapidly pre-heated under tensile stress up to 120 MPa. It was found that magnetic characteristics of the material (magnetic anisotropy energy and the core loss) can be controlled by varying the tensile stress dur...
متن کاملCorrelation between MI Effect and Transverse Anisotropy in Stress-Annealed Nanocrystalline Alloys: A Mössbauer Effect Study
In order to understand the correlation between the large and sensitive magneto-impedance (MI) effect in the tensile stress-annealed Fe-based nanocrystalline alloy Fe73.5Cu1Nb3Si13.5B9 and the transverse magnetic anisotropy on a microscopic scale, a Mössbauer effect study has been carried out. A series of ribbon samples were subject to thermal annealing with tensile stress s up to 60 MPa. MI mea...
متن کاملEffect of Heat Treatment Time on the Characteristics of Coating Formed on Nanocrystalline Finemet Foils
In the present research, amorphous Fe73.5Si13.5B9Nb3Cu1 Finemet foils, 21-26µm in thickness and 5mm in width, were prepared by Planar Flow Casting (PFC) process. Wound cores of amorphous Finemet foils were simultaneously annealed and heat treated at 540°C for 60, 120 and 240 minutes in steam and air flow to form oxide insulating coating layer on both surfaces of the foils. The structure of nano...
متن کاملSpatial detection of ferromagnetic wires using GMR sensor and based on shape induced anisotropy
The purpose of this paper is to introduce a new technique for row spacing measurement in a wire array using giant magnetoresistive (GMR) sensor. The self-rectifying property of the GMR-based probes leads to accurately detection of the magnetic field fluctuations caused by surface-breaking cracks in conductive materials, shape-induced magnetic anisotropy, etc. The ability to manufacture probes h...
متن کامل