Simultaneous Enhancement of Electrical Conductivities and Mechanical Properties in Cu-Ti Alloy by Hydrogenation Process
نویسندگان
چکیده
Effects of hydrogenation process of the microstructure, electrical conductivity and mechanical properties for the Cu-(1~3) mass%Ti alloys were investigated. During hydrogenation process at 350°C, 7.5 MPa for 48 h, the disproportionation reaction occurred with forming of Ti hydrides in the alloy. It is found that remarkable simultaneous improvements of mechanical strength of 1094 MPa and electrical properties of 21%IACS are obtained in the hydrogenated Cu-3mass%Ti alloy.
منابع مشابه
Effect of Ni on Amorphization of Ti-Cu-Ni Ternary alloys Prepared by Mechanical alloying
Amorphous alloys has been taken into consideration because of their unique properties and are nominated as the future engineering materials. In this research, the effect of Ni and milling time on amorphization process and thermal stability of Ti50Cu50-xNix(x=10, 15, 25 at%) alloy system were investigated. The evolution of amorphization during milling, thermal stability and subsequent heat treat...
متن کاملInvestigation on Mechanical and Electrical Properties of Cu-Ti Nanocomposite Produced by Mechanical Alloying
In this paper, Cu-Ti nanocomposite synthesized via ball milling of copper-titanium powders in 1, 3, and 6 of weight percentage compounds. The vial speed was 350 rpm and ball to powder weight ratio kept at 15:1 under Argon atmosphere, and the time of milling was 90 h. Obtained powders were studied by scanning electron microscopy (SEM), X-ray diffraction (XRD), and dynamic light scattering (DLS)....
متن کاملProduction of Cu-Cr-Zr Alloy Using Electro Slag Remelting Technique (RESEARCH NOTE)
This study focused on the effect of electro slag remelting process (ESR) on microstructure and composition of an as-cast alloy of Cu-Cr-Zr. These observations revealed that applying ESR process results in a more uniform distribution of alloying elements, however a slight aggregation of large precipitates and inclusions existed in as-cast ingot was found. Additionally, impurities like P, S and M...
متن کاملExperimental Evaluation of Surface Alterations Induced in Machining of Ti-6Al-4V Alloy
Surface integrity of workpieces after machining processes is one of the most essential requirements of engineers in advanced industries, since it has significant effect on performance and service life of the components. Based on this, thermal and mechanical loads generated by machining are responsible for change in mechanical properties of the machined workpiece and consequently, they should be...
متن کاملEffect of Combination on Properties of Cu-Ag Nanocomposites Synthesized by Heat Treatment
Ag-Cu solid solutions prepared via ball milling process were subsequently milled for 30 h and investigated by X-ray diffraction technique for Cu-20%Ag, Cu-3.64%Ag and Cu-80%Ag. It was noted that the solid solubility level increased by increasing initial solute content in composition. Results showed peak positions of silver and copper changed with milling time. By heating up to 700 K, ...
متن کامل