Reactive Electrophilic OI− Species Evidenced in High‐Performance Iridium Oxohydroxide Water Oxidation Electrocatalysts
نویسندگان
چکیده
Although quasi-amorphous iridium oxohydroxides have been identified repeatedly as superior electrocatalysts for the oxygen evolution reaction (OER), an exact description of the performance-relevant species has remained a challenge. In this context, we report the characterization of hydrothermally prepared iridium(III/IV) oxohydroxides that exhibit exceptional OER performances. Holes in the O 2p states of the iridium(III/IV) oxohydroxides result in reactive OI- species, which are identified by characteristic near-edge X-ray absorption fine structure (NEXAFS) features. A prototypical titration reaction with CO as a probe molecule shows that these OI- species are highly susceptible to nucleophilic attack at room temperature. Similarly to the preactivated oxygen involved in the biological OER in photosystem II, the electrophilic OI- species evidenced in the iridium(III/IV) oxohydroxides are suggested to be precursors to species involved in the O-O bond formation during the electrocatalytic OER. The CO titration also highlights a link between the OER performance and the surface/subsurface mobility of the OI- species. Thus, the superior electrocatalytic properties of the iridium (III/IV) oxohydroxides are explained by their ability to accommodate preactivated electrophilic OI- species that can migrate within the lattice.
منابع مشابه
In situ observation of reactive oxygen species forming on oxygen-evolving iridium surfaces.
Water splitting performed in acidic media relies on the exceptional performance of iridium-based materials to catalyze the oxygen evolution reaction (OER). In the present work, we use in situ X-ray photoemission and absorption spectroscopy to resolve the long-standing debate about surface species present in iridium-based catalysts during the OER. We find that the surface of an initially metalli...
متن کاملReactive oxygen species in iridium-based OER catalysts.
Tremendous effort has been devoted towards elucidating the fundamental reasons for the higher activity of hydrated amorphous IrIII/IV oxyhydroxides (IrO x ) in the oxygen evolution reaction (OER) in comparison with their crystalline counterpart, rutile-type IrO2, by focusing on the metal oxidation state. Here we demonstrate that, through an analogy to photosystem II, the nature of this reactive...
متن کاملCatalysis of water oxidation in acetonitrile by iridium oxide nanoparticles.
Water oxidation catalysed by iridium oxide nanoparticles (IrO2 NPs) in water-acetonitrile mixtures using [RuIII(bpy)3]3+ as oxidant was studied as a function of the water content, the acidity of the reaction media and the catalyst concentration. It was observed that under acidic conditions (HClO4) and at high water contents (80% (v/v)) the reaction is slow, but its rate increases as the water c...
متن کاملCatalysis of water oxidation in acetonitrile by iridium oxide nanoparticles† †Electronic supplementary information (ESI) available: Experimental methods, syntheses, characterization, details concerning the kinetic experiments. See DOI: 10.1039/c4sc02196g Click here for additional data file. Click here for additional data file.
Water oxidation catalysed by iridium oxide nanoparticles (IrO2 NPs) in water–acetonitrile mixtures using [Ru(bpy)3] 3+ as oxidant was studied as a function of the water content, the acidity of the reaction media and the catalyst concentration. It was observed that under acidic conditions (HClO4) and at high water contents (80% (v/v)) the reaction is slow, but its rate increases as the water con...
متن کاملIridium-platinum alloy nanoparticles: Composition-dependent electrocatalytic activity for formic acid oxidation†
IrxPt100 x alloy nanoparticles with varied compositions (x1⁄4 100, 75, 67, 50, 34, and 0) were synthesized by a thermolytic process at varied ratios of the IrCl3 and PtCl2 precursors. High-resolution transmission electron microscopic (HRTEM) measurements showed that the nanoparticles all exhibited well-defined crystalline structures with the average core diameters around 2 nm; and the elemental...