Effect of Surface Treatment with Er;Cr:YSSG, Nd:YAG, and CO2 Lasers on Repair Shear Bond Strength of a Silorane-based Composite Resin
نویسندگان
چکیده
Background and aims. The aim of the present study was to compare the effect ofsurface treatment with Er; Cr:YSSG, Nd:YAG, and CO2 lasers on repair shear bond strength of a silorane-based composite resin. Materials and methods. Sixty eight cylindrical samples of a silorane-based composite resin (Filtek Silorane) were pre-pared and randomly divided into 4 groups as follows: group 1: without surface treatment; groups 2, 3 and 4 with surface treatments using Er; Cr:YSSG, Nd:YAG, and CO2 lasers, respectively. A positive control group (group 5) was assigned in order to measure cohesive strength. Repair shear bond strength values were measured and data was analyzed using one-way ANOVA and a post hoc Tukey test at a significance level of α=0.05. Results. There were statistically significant differences in repair shear bond strength values between group 2 and other groups (P < 0.05); and between group 1and groups 3and 4 (P < 0.001); however, there were no significant differences be-tween groups 3 and 4 (P = 0.91). Conclusion. The repair shear bond strength of silorane-based composite resin was acceptable by surface treatment with lasers.
منابع مشابه
Effect of surface preparation with Nd:YAG and Er,Cr:YSGG lasers on the repair bond strength of lithium disilicate glass ceramic to a silorane-based composite resin
Background. This study was undertaken to evaluate the repair bond strength of lithium disilicate glass ceramic to a siloranebased composite resin after surface preparation with Nd:YAG and Er,Cr:YSGG lasers. Methods. A total of 102 lithium disilicate glass ceramic samples (IPS e.max Press), measuring 5 mm in diameter and 4 mm in thickness, were randomly assigned to 6 groups (n=17): group 1, no s...
متن کاملComparison of Shear Bond Strength of Silorane and Methacrylate-Based Composites to IPS Empress 2 Ceramic with Various Surface Treatments
Objectives: Treatment of chipped or fractured porcelain with composite resin is considered as an economic treatment for minor fractures in ceramics. The aim of this study was to evaluate the effect of different ceramic surface treatments on bond strength of methacrylate-based and silorane-based composite resin to IPS Empress 2. Methods: Sixty IPS Empress 2 ceramic discs were fabrica...
متن کاملبررسی اثر لیزر بر آمادهسازی سطح سرامیک زیرکونیا در استحکام باند برشی به عاج دندان
Background and Aims: Reliable bonding between tooth substrate and zirconia-based ceramic restorations is always of great importance. The laser might be useful for treatment of ceramic surfaces. The aim of the present study was to investigate the effect of laser irradiation on the shear bond strength of zirconia ceramic surface to dentin. Materials and Methods: In this experimental in vitro stu...
متن کاملEffect of Mechanical Surface Treatment on the Repair Bond Strength of the Silorane-based Composite Resin
Background and aims. A proper bond must be created between the existing composite resin and the new one for successful repair. The aim of this study was to compare the effect of three mechanical surface treatments, using diamond bur, air abrasion, and Er,Cr:YSGG laser, on the repair bond strength of the silorane-based composite resin. Materials and methods. Sixty cylindrical composite resin spe...
متن کاملبررسی اثر آماده سازی سطح یک نوع کامپوزیت غیرمستقیم، به وسیله دو نوع لیزرNd:YAG و Er:YAG و اسید اچ، بر استحکام باند ریز برشی سمان رزینی
Introduction: In order to increase the bonding strength of the composite resin cements to the indirect composites, experiments such as the creation of surface roughness with sandblasting, acid-etching, silane application, laser, etc. have been carried out. However, there is no consensus about the results. Therefore, the purpose of this study was to investigate the effect of Er: YAG and Nd: YAG ...