Electrochemical Study of the Corrosion Performance of AISI- 309 and AISI-310 Exposed in NaVO3 at High Temperature
نویسندگان
چکیده
1 FCQeI-CIICAp-Universidad Autónoma del Estado de Morelos, Av. Universidad 1001, Col. Chamilpa, C.P. 62210, Cuernavaca, Morelos, México. 2 Instituto de Investigaciones Eléctricas, Reforma 113, Col. Palmira, C.P. 62490, Cuernavaca, Morelos, México. 3 Instituto de Ciencias Físicas, Universidad Nacional Autónoma de México, Avenida Universidad s/n, 62210, Cuernavaca, Morelos, México. Corrosión y Protección (CyP), Buffon 46, 11590 México City, DF, México * E-mail: [email protected]
منابع مشابه
Effect of bonding temperature on the microstructure and electrochemical corrosion behavior of TLP bonded AISI 304L stainless steel
Transient liquid phase (TLP) bonding of AISI 304L stainless steel was carried out using BNi-2 amorphous interlayer. The microstructure of the joint area was studied by using optical and scanning electron microscopes and energy dispersive spectroscopy. The effect of bonding temperature (1030-1110 °C) was studied on the microstructure and corrosion behavior of the TLP bonded samples. Electrochemi...
متن کاملEffect of bonding temperature on the microstructure and electrochemical corrosion behavior of TLP bonded AISI 304L stainless steel
Transient liquid phase (TLP) bonding of AISI 304L stainless steel was carried out using BNi-2 amorphous interlayer. The microstructure of the joint area was studied by using optical and scanning electron microscopes and energy dispersive spectroscopy. The effect of bonding temperature (1030-1110 °C) was studied on the microstructure and corrosion behavior of the TLP bonded samples. Electrochemi...
متن کاملCorrosion Behaviour of Nickel Coated AISI 316 Stainless Steel as a Function of Annealing Temperature
AISI 316 stainless steels were coated with 250 nm Ni film by electron beam deposition and post-annealed at different temperatures with a nitrogen flow of 600 cm3min-1 nitrogen. The prepared samples were corrosion tested in 1.0 M sulphuric acid solution using potentiodynamic technique. Crystallographic and morphological structure of the samples were analyzedanalysed by X-ray diffraction (XRD) an...
متن کاملCorrosion Performance of Austenitic Stainless Steel Bipolar Plates for Nafion- and Room-Temperature Ionic-Liquid-Based PEMFCs
In this paper we study the corrosion of AISI 304 austenitic stainless steel PEMFC bipolar plates in aqueous and room-temperature ionic-liquid electrolytes. The anodic potential thresholds and dynamics have been investigated by electrochemical (potentiodynamic and potentiostatic) and in situ spectroelectrochemical methods (visible electroreflectance and VIS-UV spectroellipsometry). We measured t...
متن کاملPassivity of AISI 316L stainless steel as a function of nitric concentration
In this study, electrochemical behaviour of passive films formed on AISI 316L stainless steel (AISI 316L) in three acidic solutions concentrations (0.3, 0.6, and 0.9M HNO3) under open circuit potential conditions were evaluated by potentiodynamic polarization, Mott–Schottky analysis and electrochemical impedance spectroscopy (EIS) techniques. The potentiodynamic polarization results showed that...
متن کامل