The aim of this study was to evaluate the effect of acetic NaF solutions on fluoride-containing restorative materials. As the pH value of solution decreased, the degree of microhardness change in restorative materials increased- regardless of product. Dyract AP (DA) and F2000 (F2) (polyacid-modified resin composites) showed the greatest decrease in microhardness after immersion for three days. Similarly, as the pH value decreased, volumetric weight change (loss) increased in all products. DA and F2 showed the greatest--but similar-weight change in pH 3.5 solution among the products. In terms of color change, most specimens showed a slight color change after immersion for one and three days-regardless of pH value. However, F2 in pH 3.5 solution showed a noticeable color change (deltaE*=2.1). In terms of surface morphology, specimens in distilled water showed only minor surface modification. However, in pH 3.5 solution, DA and F2 showed randomly propagating cracks, while Solitaire 2 and Tetric Ceram (resin composites) lost many fillers less than 2 microm in size.
منابع مشابه
Effects of polysiloxane coating of NaF on the release profile of fluoride ion from Bis-GMA/TEGDMA resin containing NaF.
The aim of this study was to regulate fluoride release from restorative resin containing NaF using N-(beta-aminoethyl)-gamma-aminopropylmethyldimethoxysilane (AMMS) and evaluate factors that regulate fluoride release from the resin. ESCA analysis, FT-IR measurements along with SEM observations demonstrated that a polysiloxane layer was formed on the surface of NaF treated with AMMS. Bis-GMA/TEG...
متن کاملSodium fluoride addition to a two-step etch-and-rinse adhesive system: effect on dentin microtensile bond strength and durability
Introduction: Studies have suggested that sodium fluoride (NaF) has an inhibitory effect on the activity of endogenous matrix metalloproteinase enzymes. This study assessed the effect of a fluoride-containing adhesive on microtensile bond strength (µTBS) over time. Material & Methods: In this experimental study, 36 extracted third molars were used to evaluate the µTBS of...
متن کاملEffect of acetic NaF solution on the corrosion behavior of stainless steel orthodontic brackets.
This study assessed the effect of acetic NaF solutions on stainless steel orthodontic brackets. Acetic acid was added to a 0.1% NaF solution to make two solutions, one with pH 3.5 and the other with pH 6. For the two different stainless steel brackets (Tomy, Dentaurum) used in this study, they had a similar elemental composition--except with Mo (molybdenum) in the Tomy bracket. The brackets wer...
متن کاملCariostatic effect of fluoride-containing restorative materials associated with fluoride gels on root dentin
UNLABELLED Secondary caries is still the main cause of restoration replacement, especially on the root surface. OBJECTIVE This in vitro study evaluated the cariostatic effects of fluoride-containing restorative materials associated with fluoride gels, on root dentin. MATERIALS AND METHODS A randomized complete block design was used to test the effects of the restorative systems, fluoride re...
متن کاملAntibacterial activity against Streptococcus mutans and inhibition of bacterial induced enamel demineralization of propolis, miswak, and chitosan nanoparticles based dental varnishes
Using natural products can be a cost-effective approach for caries prevention especially in low income countries where dental caries is highly prevalent and the resources are limited. Specially prepared dental varnishes containing propolis, miswak, and chitosan nanoparticles (CS-NPs) with or without sodium fluoride (NaF) were assessed for antibacterial effect against Streptococcus mutans (S. mu...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Dental materials journal
دوره 26 1 شماره
صفحات -
تاریخ انتشار 2007