Experiment of enhancing critical current in Bi-2223/Ag tape by means of ferromagnetic shielding

نویسندگان

  • A.K.M. Alamgir
  • C. Gu
  • Z. Han
چکیده

Critical current in multifilamentary Ag-sheath Bi-2223 tape is enhanced to some extent by means of thin and narrow coating of pure nickel. The concept of enhancing critical current is based on the magnetic shielding effect resulting in redirection of self-field flux lines. The Ni coating was introduced at the edge regime of the tape in order to redirect the perpendicular component of self-field lines which is severe at the edges. Critical current in a typical Ag-sheath Bi-2223 tape was enhanced up to 11% by 50 lm thick and 0.4 mm long Ni coating without any change of self-field loss. This fact reveals that additional ferromagnetic loss could be compensated by the shielding effect and increased critical current of the tape. The degree of enhancement in critical current as well as ferromagnetic impact on ac losses depend on the length and thickness of ferromagnetic coating introduced. Therefore, it is very important to control the geometry of ferromagnetic coating in order to balance the critical current and ac loss for optimum superconductor performance. Introduction of ferromagnetic coating and its effect on electromagnetic properties in multifilamentary Bi-2223/Ag tape will be reported in this article. 2005 Elsevier B.V. All rights reserved. PACS: 41.20.Gz; 74.25.Gz

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Observation of vortex distribution in samples of Bi-2223 Ag-sheathed tapes with and without uranium doping by means of the high-resolution Bitter method

We examined the distribution of vortices in both Bi-2223 Ag-sheathed tape and U-doped Bi-2223 Ag-sheathed tape applying the high-resolution Bitter method. In the low temperature region ( ), we found that the vortices in the undoped Bi-2223 Ag-sheathed tape developed into either a triangular arrangement or a heterogeneous arrangement along the grain boundaries of the Ag sheath, which form weak p...

متن کامل

تأثیر آلایش نقره بر خواص ساختاری، الکتریکی و مغناطیسی سیم ابررسانای Bi/Ag 2223

 In this study, the superconducting properties of Bi-2223/Ag wires, made by the PIT method have been studied. Powder samples were prepared using conventional solid state reaction method. After calcination, samples with different Ag percent (0, 5, 10, 15, 20, and 25) prepared and sintered at 830 °C. It was shown that Ag addition has not only affected the formation of the desired Bi-2223 phase an...

متن کامل

Magnetic Shield Using a Bi-2223 High-Temperature Super- conductor

Katsumi Ohata* Junichi Sato* ABSTRACT: Magnetic shielding for strong magnets using a high-temperature superconductor that can be operated at liquid nitrogen temperature has been studied. Long and large-cross-section (9 mm wide and 0.5 mm thick) 54-filament Bi-2223/Ag tape was developed. Double pancake coils were wound using the tapes having sufficient bending strain tolerance for the react-and-...

متن کامل

The Current Distribution in Bi-2223/Ag HTS Conductors: Comparing Hall Probe and Magnetic Knife

We analyzed the current distribution in three Bi-2223/Ag tapes with different filament lay-out, comparing the results of magnetic knife and Hall probe experiments. Detailed knowledge of the current distribution can be useful for the diagnostics of HTS conductors. The lateral current distribution was measured with the non-destructive magnetic knife technique and used to calculate the correspondi...

متن کامل

ساخت و بررسی تأثیر نانوذرات Sb2O3 بر ابررسانای 2223 – Bi

In this paper Sb2O3 nanoparticles are synthesized by solution method. The effect of these nanoparticles on the Bi-2223 superconductor properties has been investigated. The critical temperature, critical current density and activation energy were measured by the standard four-probe method. Magnetic properties of the samples were measured by using the AC magnetic susceptibility. The microstructur...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2005