Erosion process of a glass ionomer cement in organic acids.

نویسندگان

  • S Matsuya
  • Y Matsuya
  • Y Yamamoto
  • M Yamane
چکیده

Erosion of a glass ionomer cement in acetic (AA), lactic (LA), citric (CA) and hydrochloric acids (HA) was investigated by means of chemical analysis, SEM observation and infrared (IR) spectroscopy. The larger stability constants of the complex between the acid anions and Al or Ca, or the lower the pH of the acid solutions, the more Al, Ca, Na, Si and F were leached. SEM observation revealed that the cement matrix dissolved out in 0.01M CA and HA. White precipitates formed in 0.01M CA and HA after immersion of the cement. They were identified as hydrated silicious gels by IR spectroscopy

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

The Effect of Cigarette Smoking on Solubility and Disintegration of Resin Modified Glass Ionomer Cement – An In Vitro Study

Introduction: Glass ionomer cement (GIC) is a dental restorative material that is prone to solubility and degradation. GIC could degrade in presence of water and desiccation due to environmental factors during setting process and eventually might lead to the failure of the restoration. Cigarette smoking brings a complex chemical mixture to oral cavity that can inhibit polymeriz...

متن کامل

Susceptibility of restorations and adjacent enamel/dentine to erosion under different salivary flow conditions.

OBJECTIVES The aim of this study was to investigate the effect of erosion on direct tooth-coloured restorations and adjacent enamel/dentine under low and normal simulated salivary flow rates. METHODS Bovine enamel and dentine specimens were prepared (n=16) and restored with the following materials: resin composite (FiltekZ250), resin-modified glass ionomer cement (Fuji II LC), high-viscosity ...

متن کامل

Reinforcement of Glass Ionomer Cement: Incorporating with Silk Fiber

The aim of this study was to synthesis of glass ionomer-silk fiber composite and to evaluate the effect of adding natural degummed silk fiber on the mechanical properties of glass ionomer cement (GIC). For this purpose, natural degummed silk fibers with 1 mm in length and 13-16 µm in diameter were added to the ceramic component of a commercial glass ionomer cement in 1, 3 and 5 wt. %. Compressi...

متن کامل

Comparison of the solubility of three resin cements and a resin-modified glass ionomer cement: An in vitro study

Background and aims: Solubility is an important property of luting cements in determining clinical durability. The aim of this study was to compare the solubility of Panavia, Calibra and Maxcem resin cements with that of GC Fuji PLUS resin modified glass ionomer cement in three different pH values. Materials and Methods: A total of 96 specimens were prepared (8mm diameter, 4mm thickness) accor...

متن کامل

Shear bond strength evaluation of resin composite to resin-modified glass-ionomer cement using three different resin adhesives vs. glass-ionomer based adhesive

Background: The clinical success of sandwich technique depends on the strength of resin-modified glass ionomer cement (RMGIC) bonding to both dentin and resin composite. Therefore, the shear bond strength (SBS) of resin composite bonded to RMGIC utilizing different resin adhesives versus a GIC-based adhesive was compared. Materials and methods: In this in vitro study, 84 holes (5×2 mm) were pre...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:
  • Dental materials journal

دوره 3 2  شماره 

صفحات  -

تاریخ انتشار 1984