Comparative Evaluation of the Effects of Light Intensities and Curing Cycles of QTH, and LED Lights on Microleakage of Class V Composite Restorations.
نویسندگان
چکیده
BACKGROUND The purpose of this study was to evaluate the effects of light intensity and curing cycles of QTH and LED lights on the microleakage of Class V composite restorations. MATERIALS AND METHODS Eighty freshly extracted human maxillary premolars were used for this study. Standardized Class V cavities were prepared and they were restored with microhybrid resin composite. According to the curing protocol, the teeth were then divided into 4 groups (n=20): QTH curing (standard and soft start modes), and LED (standard and soft start modes) irradiations. Microleakage was evaluated by immersion of the samples in 50% silver nitrate solution. The samples were then sectioned, evaluated under a stereomicroscope, and scored for microleakage. RESULTS The results of the present in-vitro study showed mean dye leakage scores of 1.9, 1.2, 1.45 and 0.90 for Group I (QTH-Standard mode), Group II (QTH-Soft Start mode), Group III (LED-Standard mode) and Group IV (LED-Soft Start mode) respectively. CONCLUSION It was thus concluded that the soft start polymerization showed a highly significant difference as compared to the standard curing modes of QTH and LED lights, respectively.
منابع مشابه
Effect of Three Light Curing Protocols and Load Cycling on Microleakage of Class V Composite Restorations
Objective: Different methods have been suggested to overcome the polymerization shrinkage of composite restorations. Changing the light curing protocol to improve polymerization by using new light curing units is among these methods. The new devices are more efficient, portable and durable and produce less heat. This study aimed to assess the marginal microleakage of class V composite restora...
متن کاملThe effect of three different curing methods on the microleakage of cl V posterior composite restorations
The effect of three different curing methods on the microleakage of cl V posterior composite restorations Dr. N. Mohammadi* - Dr. P. Alizadeh Oskoee* - Dr. S. Savadi Oskoee*- Dr. A . Soleyman zadeh** *- Assistant Professor of Esthetic & Operative Dentistry Dept. - Faculty of Dentistry – Tabriz University of Medical Sciences.*- Dentist. Background and Aim: Light-cured composites have become almo...
متن کاملThe Effect of Different Bonding Agent Curing Times on Microleakage of Composite Restorations in Enamel and Dentin Mar- gins Using Two Curing Systems
Received: 26 July 2011 Accepted: 17 July 2012 Abstract Background and Aim: Lack of appropriate seal is one of the major problems in composite restorations. Properties of the bonding system can play a crucial role in sealing ability of these restorations. The aim of this study was to evaluate the microleakage of class V composite restorations with varying irradiation times for curing dentin bond...
متن کاملComparison of the Effect of Three LED Light Modes and Conventional QTH Curing Light on Shear Bond Strength of Composite to Dentin
Objective: Shear bond strength is an important property inherent to the durability of tooth-colored restorative materials namely composite resins. It has been years that halogen light sources have been used for polymerization of composite resins. In recent years Light Emitting Diodes (LED) have been introduced for this purpose. With respect to their longer bulb life, needless of a filter and ...
متن کاملمقایسه تأثیر دو نوع دستگاه لایت کیور با مدهای مختلف بر میزان میکرولیکیج ترمیمهای کلاس II کامپوزیتی
Background and Aims: One of the main disadvantages of light cured composite resin materials is polymerization shrinkage upon curing. This leads to the microleakage of restoration and finally failure of the restoration. The purpose of this study was to investigate the effect of two types of light curing devices with different modes on the microleakage of posterior composite filling in ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Journal of clinical and diagnostic research : JCDR
دوره 8 3 شماره
صفحات -
تاریخ انتشار 2014