Orientation and Phase Relationships between Titania Films and Polycrystalline BaTiO3 Substrates as Determined by Electron Backscatter Diffraction Mapping
نویسندگان
چکیده
Titania films have been grown on polycrystalline BaTiO3 (BTO) substrates at 7001C by pulsed laser deposition. Electron backscatter diffraction (EBSD) was used to determine grain orientations in the substrate before growth, and the phase and orientation of the supported films after growth. All BaTiO3 grains within 261 of (001) were covered by anatase films with an orientation relationship of (001)Anatase||(001)BTO and [100]Anatase ||[100]BTO. Rutile with a variety of orientations grew on BaTiO3 grains with orientations closer to (110) and (111). EBSD mapping provides an efficient means for determining phase and orientation relationships of films over all orientation parameters.
منابع مشابه
Band-Gap Tuning Of Electron Beam Evaporated Cds Thin Films
The effect of evaporation rate on structural, morphological and optical properties of electron beam evaporated CdS thin films have been investigated. CdS thin film deposited by electron beam evaporation method in 12nm/min and 60nm/min evaporation rates on glass substrates. X-ray diffraction, scanning electron microscopy, UV-Vis-NIR spectroscopy and Atomic Force Microscopy were used to character...
متن کاملPhotochemical Reactivity of Titania Films on BaTiO3 Substrates: Influence of Titania Phase and Orientation
Titania films were grown on BaTiO3 (BTO) substrates by pulsed laser deposition to create (001)Anatase||(100)BTO, (100)Rutile||(111)BTO, and (110)Rutile||(110)BTO heterostructures. The photochemical reactivity was evaluated by observing the amount of silver reduced by each film under identical conditions. The thickest films (100 nm) had reactivities that varied with the phase of titania and the ...
متن کاملEffect of morphology and nonbounded interface on dielectric properties of plasma sprayed BaTiO3 Coating
In this research, BaTiO3 thick deposit has been successfully sprayed by air plasma spray. The microstructure and dielectric properties of thick films were investigated by secondary electron microscopy (SEM) and LCR meter respectively. XRD measurement was carried out on plasma sprayed BaTiO3. The results illustrate differences in the crystal structure between plasma sprayed coatings and feed sto...
متن کاملThe Effect of thickness parameter and Fluorine Dopant on Photocatalytic performance of TiO2 thin films
In this study, Pure and doped titania sols with Fluorine (F/Ti:0.06) dopant, were prepared by sol-gel method and Ammonium Fluoride(NH4F) as the precursor. They were deposited on glass substrates (soda lime) in a certain(optimum) nanometric thickness by the dip coating method. Coated samples were dried and calcined under the specific rate. Phase composition and optical properties of coatings wer...
متن کاملNano-structural Characterization of Post-annealed ZnO Thin Films by X-ray Diffraction and Field Emission Scanning Electron Microscopy
ZnO thin films were deposited on Si(400) substrates by e-beam evaporation technique, and then post-annealed at different annealing temperatures (200-800°C). Dependence of the crystallographic structure, nano-strain, chemical composition and surface physical Morphology of these layers on annealing temperature were studied. The crystallographic structure of films was studied using X-Ray Diffracti...
متن کامل