An in vitro study of different material properties of Biodentine compared to ProRoot MTA

نویسندگان

  • Markus Kaup
  • Edgar Schäfer
  • Till Dammaschke
چکیده

INTRODUCTION The aim of this study was to compare solubility, microhardness, radiopacity, and setting time of Biodentine with ProRoot MTA. METHODS Solubility in distilled water, radioopacity, and setting time were evaluated in accordance with International Standard ISO 6876:2001. In addition, the solubility in Phosphate Buffered Saline (PBS) buffer was determined. For microhardness-testing, ten samples of each cement were produced. All samples were loaded with a diamond indenter point with a weight of 100 g for 30s. All data were analysed using the Student-t-test. RESULTS Both materials fulfilled the requirements of the International Standard ISO 6876:2001 and showed a solubility of <3% after 24 h. At all exposure times Biodentine was significantly more soluble than ProRoot MTA (p < 0.0001). After immersion in PBS-buffer a precipitation of hydroxyapatite was visible. The Vickers microhardness for Biodentine was significantly higher (62.35 ± 11.55HV) compared with ProRoot MTA (26.93 ± 4.66HV) (p < 0.0001). ProRoot MTA was significantly more radiopaque (6.40 ± 0.06 mm Al) than Biodentine (1.50 ± 0.10 mm Al) (p < 0.0001). The setting time for Biodentine (85.66 ± 6.03 min) was significantly lower than for ProRoot MTA (228.33 ± 2.88 min) (p < 0.0001). CONCLUSIONS Biodentine and ProRoot MTA displayed different material properties. The solubility of both cements was in accordance with the International Standard ISO 6876:2001, whereas ProRoot MTA showed a significantly lower solubility. With regard to microhardness, Biodentine may be used to replace dentine. The radioopacity of Biodentine did not fulfil the requirements laid down in the International Standard ISO 6876:2001. The setting time for ProRoot MTA is significantly higher. Both materials can be used in different indications where specific material properties may be favourable. Hence, the here tested material properties are of clinical relevance.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

In vitro cytotoxicity of four calcium silicate-based endodontic cements on human monocytes, a colorimetric MTT assay

OBJECTIVES This study was performed to evaluate the cytotoxicity of four calcium silicate-based endodontic cements at different storage times after mixing. MATERIALS AND METHODS Capillary tubes were filled with Biodentine (Septodont), Calcium Enriched Mixture (CEM cement, BioniqueDent), Tech Biosealer Endo (Tech Biosealer) and ProRoot MTA (Dentsply Tulsa Dental). Empty tubes and tubes contain...

متن کامل

In Vitro Screening of the Apatite-Forming Ability, Biointeractivity and Physical Properties of a Tricalcium Silicate Material for Endodontics and Restorative Dentistry

Aim: Calcium silicate-based materials are hydraulic self-setting materials with physico-chemical properties suitable for endodontic surgery and good biological/clinical outcomes. The study aim was to evaluate the bio-properties (biointeractivity and apatite-forming ability) and selected physical properties (porosity, water sorption, solubility, and setting time) of Biodentine, a tricalcium sili...

متن کامل

The effect of blood contamination on dislocation resistance of different endodontic reparative materials.

This study evaluated the retention characteristics of ProRoot mineral trioxide aggregate (MTA), RetroMTA, Supra MTA, and Biodentine biomaterials used to repair furcation perforations contaminated with blood. Furcal perforations measuring 1.3 mm in diameter and 2 mm in height were created in 96 mandibular first molar teeth, which were then randomly divided into the following two groups (n = 48):...

متن کامل

Evaluation of reparative dentin formation of ProRoot MTA, Biodentine and BioAggregate using micro-CT and immunohistochemistry.

OBJECTIVES The purpose of this study was to assess the ability of two new calcium silicate-based pulp-capping materials (Biodentine and BioAggregate) to induce healing in a rat pulp injury model and to compare them with mineral trioxide aggregate (MTA). MATERIALS AND METHODS Eighteen rats were anesthetized, cavities were prepared and the pulp was capped with either of ProRoot MTA, Biodentine,...

متن کامل

Effect of Blood Exposure on Push-Out Bond Strength of Four Calcium Silicate Based Cements

INTRODUCTION The purpose of this study was to compare the push-out bond strength of white ProRoot Mineral Trioxide Aggregate (MTA), Biodentine, calcium-enriched mixture (CEM) cement and Endosequence Root Repair Material (ERRM) putty after exposure to blood. METHODS AND MATERIALS A total of 96 root dentin slices with a standardized thickness of 1.00±0.05 mm and standardized canal spaces were r...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 11  شماره 

صفحات  -

تاریخ انتشار 2015