SOFT MAGNETIC PROPERTIES OF CoFeBSi AMORPHOUS RIBBON IMPROVED BY PULSE ANNEALING
نویسندگان
چکیده
منابع مشابه
بررسی سینتیک نانو تبلور نوارهای نرم مغناطیس FINEMET در شرایط غیرهمدما
The soft magnetic nanocrystalline Fe73.5Si13.5B9Cu1Nb3 alloy (FINEMET®) is produced by heat treatment of amorphous precursor. Determining kinetic parameters of amorphous structure transformation to nanocrystalline allows the control of microstructure (e.g. size and volume fraction of nanocrystalline grains) in order to achieve desired soft magnetic properties by optimizing the heat treatment co...
متن کاملNanocrystallization in Co67Cr7Fe4Si8B14 Amorphous Alloy Ribbons
The nanocrystallization of Co67Fe4Cr7Si8B14 amorphous ribbons which prepared by planar flow melt spinning process (PFMS) was investigated. Crystallization of the ribbons was studied by differential thermal analysis (DTA), X-ray diffraction (XRD) and transmission electron microscopy (TEM). The DTA result of amorphous ribbon at heating rate of 10˚C/min showedoccurrence of phase transitions in two...
متن کاملIntroducing and investigating structural and magnetic properties of ribbons Co68.5-xFe4WxSi16.5B11 (x = 0.8, 2) in amorphous and crystalline states
In this study, for the first time, cobalt base ribbons were made by adding two different amounts of tungsten with Co67.7Fe4W0.8Si16.5B11 and Co66.5Fe4W2 Si16.5B11 compounds by melt spinning in the water. The pattern of X-ray diffraction taken from these ribbons shows that these magnetic ribbons are amorphous. By using thermal analysis curves, taken from the ribbons, crystallization temperature...
متن کاملCoFe Layers Thickness and Annealing Effect on the Magnetic Behavior of the CoFe/Cu Multilayer Nanowires
CoFe/Cu multilayer nanowires were electrodeposited into anodic aluminum oxide templates prepared by a two-step mild anodization method, using the single-bath technique. Nanowires with 30 nm diameter and the definite lengths were obtained. The effect of CoFe layers thickness and annealing on the magnetic behavior of the multilayer nanowires was investigated. The layers thickness was controlled t...
متن کاملInvestigations of Magnetic Properties Through Electrodeposition Current and Controlled Cu Content in Pulse Electrodeposited CoFeCu Nanowires
CoFeCu nanowires were deposited by pulsed electrodeposition technique into the porous alumina templates by a two-step mild anodization technique, using the single-bath method. The electrodeposition was performed in a constant electrolyte while Cu constant was controlled by electrodeposition current. The electrodeposition current was 3.5, 4.25, 5 and 6 mA. The effect of electrodeposition current...