Effect of Die Materials on the Fracture Resistance of CAD/CAM Monolithic Crown Restorations
نویسندگان
چکیده
The effect of the die materials on the fracture strength of CAD/CAM monolithic ceramic crowns was studied in this research. Three different types of die materials (dentin, Ni-Cr alloy, epoxy resin) were prepared. The monolithic crowns were fabricated using a CAD/CAM System; CEREC 4. The CAD/CAM crowns were cemented to dies using a resin cement. The specimens were tested under compressive load at a crosshead speed of 1 mm/min using a universal testing machine until fracture occurred. Recorded data were statistically analyzed using one-way analysis of variance and LSD Post hoc tests (p=0.05). While CAD/CAM crowns on Ni-Cr alloy dies showed the highest fracture resistance values, CAD/CAM crowns on dentin dies showed the lowest fracture resistance values. There is no significant difference between groups statistically. Ni-Cr alloy and epoxy resin dies could be used alternatively instead of teeth for in vitro studies.
منابع مشابه
The Effect of Different Marginal Designs on the Fracture Resistance of Monolithic Zirconia Crowns
Abstract Background and Aim: One of the major problems of all ceramic restorations is their probable fracture against the occlusal force. The aim of the present in vitro study is to compare the effect of three marginal designs (shoulder, sloped shoulder, chamfer) on the fracture resistance of monolithic zirconia crowns. Materials and methods: In this in vitro study, three PEEK dies with cham...
متن کاملEffect of cements on fracture resistance of monolithic zirconia crowns
Objectives The present study investigated the effect of cements on fracture resistance of monolithic zirconia crowns in relation to their compressive strength. Materials and methods Four different cements were tested: zinc phosphate cement (ZPC), glass-ionomer cement (GIC), self-adhesive resin-based cement (SRC) and resin-based cement (RC). RC was used in both dual cure mode (RC-D) and chemical...
متن کاملEffect of marginal design on fracture resistance of IPS e.maxall ceramic restorations: Chamfer versus shoulder finish lines
Background and Aim: One of the problems of all ceramic restorations is their risk of fracture due to occlusal loads. The aim of the present study was to compare the effect of two marginal designs (shoulder and chamfer) on the fracture resistance of IPS-emax all ceramic restorations. Materials and Methods: One extracted maxillary first premolar received chamfer 50' marginal preparation (0.8 m...
متن کاملChairside Fabrication of an All-Ceramic Partial Crown Using a Zirconia-Reinforced Lithium Silicate Ceramic
The chairside fabrication of a monolithic partial crown using a zirconia-reinforced lithium silicate (ZLS) ceramic is described. The fully digitized model-free workflow in a dental practice is possible due to the use of a powder-free intraoral scanner and the computer-aided design/computer-assisted manufacturing (CAD/CAM) of the restorations. The innovative ZLS material offers a singular combin...
متن کاملIn Vitro Evaluation of Fracture Resistance of Zirconia Restorations Veneered by Two Different Systems: Rapid Layer Technique and Zir/CAD/CAM
Background: This study aimed to assess the fracture resistance of zirconia restorations fabricated with rapid layer (RL group) technique and zirconia computer-aided design/computer-aided manufacturing (zir/CAD/CAM) system (ZC group). Methods:This study evaluated 30 all-ceramic crowns in two groups of 15. After fabricating the metal dies and scanning them ...
متن کامل