Ion-Exchange in Glass-Ceramics
نویسندگان
چکیده
In the past few years, ion-exchange (IOX) in glasses has found a renewed interest with a lot of new development and research in industrial and academic labs and the commercialization of materials with outstanding mechanical properties. These glasses are now widely used in many electronic devices, including hand-held displays and tablets. The exchange is generally conducted in a bath of molten salt below the transition temperature of the glass. The exchange at the surface of an alkali ion by a bigger one brings compressive stress at the surface. The mechanical properties are dependent on the stress level at the surface and the depth of penetration of the bigger ion. As compared to glasses, glass-ceramics have the interest to display a wide range of aspects (transparent to opaque) and different mechanical properties (especially higher modulus and toughness). There has been little research on IOX in glass-ceramics. In these materials, the mechanisms are much more complex than in glasses because of their polyphasic nature: IOX generally takes place mostly in one phase (crystalline phase or residual glass). The mechanism can be similar to what is observed in glasses with the replacement of an ion by another in the structure. But in some cases this IOX leads to microstructural modifications (for example, amorphization or phase change). This article reviews these IOX mechanisms using several transparent and opaque aluminosilicate glass-ceramics as examples. The effect of the IOX in the various glass-ceramics will be described, with particular emphasis on flexural strength.
منابع مشابه
Fabrication of Na2FeP2O7 glass-ceramics for sodium ion battery
New cathode candidate Na2FeP2O7 for rechargeable sodium ion second battery was successfully prepared by glass-ceramics method. The precursor glass, which is same composition in Na2FeP2O7, was prepared by melt-quenching method. Na2FeP2O7 was obtained by heat treatment of precursor glass powder with 10% glucose addition as reduction agent of Fe3+ at 620°C for 3 h in electric furnace. Na2FeP2O7 ha...
متن کاملبررسی تاثیر پدیده تبادل یونی (Ion exchange) بر روی استحکام خمشی پرسلن سرامکو II و پرسلن Colorlogic Venner
The major foible of dental ceramics is their brittle nature. Therefore, the producers of these materials have focused on the “strength” issue. A method of increasing strength is ion exchange on porcelain surface which leads to formation of a compressive crust that opposing forces should overcome before developing a crack. In current study, ion exchange in two types of porcelain, Ceramco II wh...
متن کاملساخت شیشه- سرامیک هادی یون لیتیوم با هدایت یونی بالا برای ساخت باتریهای لیتیوم- اکسیژن و یون- لیتیوم تمام جامد
In this research, new lithium ion conductor glass-ceramics with NASICON-type structure (Li1+x+yAlxCryGe2-x-y (PO4)3, x+y=0.5) were synthesized using melt-quenching method and converted to glass-ceramics through heat treatment. Influence of addition of different concentrations of aluminum and chromium in LiGe2(PO4)3 glass-ceramic was investigated for ionic conduction improvement. Substitution of...
متن کاملPreparation, characterization and stability of Li-ion conducting Li1.5Al0.5Ge1.5(PO4)3 glass-ceramic with NASICON-type structure
A conducting lithium aluminum germanium phosphate (LAGP) glass-ceramic with a formula of Li1.5Al0.5Ge1.5(PO4)3 was synthesized by melt-quenching method and subsequent crystallization at 850 °C for 8 h. The prepared glass-ceramic was characterized using differential scanning calorimetry (DSC), X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), and AC impedance techniqu...