A new corrosion protection coating with polyaniline–TiO2 composite for steel

Organic coating strategies for corrosion protection with inherently conducting polymers have become important because of restriction on the use f heavy metals and chromates in coatings due to their environmental problems. This work presents the synthesis of polyaniline–TiO2 composites PTC) and the corrosion protection behaviour of PTC containing coating on steel. PTC was prepared by chemical oxidation of aniline and TiO2 y ammonium persulfate in phosphoric acid medium. The PTC was characterized by FTIR, XRD and SEM techniques. Suitable coating with TC was formed on steel using acrylic resin. Using electrochemical impedance spectroscopy, the PTC containing coating’s behaviour in 3% NaCl mmersion test and salt spray test has been found out. Results indicate that the coating containing PTC is able to maintain the potential of steel in assive region due to its redox property. The resistance of the coating containing PTC was more than 107 cm2 in 3% NaCl solution after 60 days nd 109 cm2 in the salt spray test of 35 days. But the resistance of the TiO2 containing coating was found to be less than 104 cm2 in both the ases. The high performance of PTC containing coating is attributed to the passivation of steel by polyaniline. 2006 Elsevier Ltd. All rights reserved.