Flexible thermoplastic composite of Polyvinyl Butyral (PVB) and waste of rigid Polyurethane foam
نویسندگان
چکیده
This study reports the preparation and characterization of composites with recycled poly(vinyl butyral) (PVB) and residue of rigid polyurethane foam (PUr), with PUr contents of 20, 35 and 50 wt %, using an extruder equipped with a Maillefer single screw and injection molding. The components of the composites were thermally characterized using differential scanning calorimetry (DSC) and thermogravimetry. The composites were evaluated by melt flow index (MFI), tensile and hardness mechanical tests and scanning electron microscopy (SEM). Tg determined by DSC of PVB sample (53 °C) indicated the presence of plasticizer (Tg of pure PVB is 70 °C). MFI of the composites indicated a viscosity increase with the PUr content and, as the shear rate was held constant during injection molding, higher viscosities promoted higher shear stresses in the composites, thereby causing breaking or tearing of the PUr particles. The SEM micrographs showed low adhesion between PVB and PUr and the presence of voids, both inherent in the rigid foam and in the interphase PVB-PUr. The SEM micrographs also showed that PVB/PUr (50/50) composite exhibited the smallest particle size and a more homogeneous and compact structure with fewer voids in the interface. The stiffness of the composites increases with addition of the PUr particles, as evidenced in the mechanical tests.
منابع مشابه
Non-Isothermal Degradation Kinetics of High Energy Protons Irradiated Polyvinyl Butyral
This research is aimed to undertake a comparative study on stability and thermal degradation kinetics of un-irradiated and high energy protons irradiated polyvinyl butyral (PVB) based on weight loss analysis and non-isothermal approaches. The weight loss by the un-irradiated PVB upon heating was found to be in two stages but due to high energy protons accelerated exposure following by chemical ...
متن کاملInhibition effect of polyvinyl butyral on crystallization of polypropylene
In this work, a series of polypropylene/polyvinyl butyral (PP/PVB) blends were prepared by melt-blending process, at PVB loadings 3 wt%, 10 wt%, and 30 wt%. The effects of PVB on crystallization behavior of PP were investigated by differential scanning calorimetry (DSC), and polarized optical microscopy (POM). The isothermal crystallization kinetics were analyzed by Avrami equations. It was fou...
متن کاملUsing A Range of PVB Spinning Solution to Acquire Diverse Morphology for Electrospun Nanofibres
Morphological changes in Polyvinyl Butyral (PVB) electrospun nanofibres can be acquired by preparation of PVB spinning solution in different solvents. Accordingly, three solvents, including ethyl alcohol, n-butanol and isopropanol, with diverse physical properties (e.g. boiling point, density, dipole moment and dielectric constant) were used to prepare PolyVinyl Butyral (PVB) spin...
متن کاملHigh Sensitive Sensor Fabricated by Reduced Graphene Oxide/Polyvinyl Butyral Nanofibers for Detecting Cu (II) in Water
Graphene oxide (GO)/polyvinyl butyral (PVB) nanofibers were prepared by a simple electrospinning technique with PVB as matrix and GO as a functional nanomaterial. GO/PVB nanofibers on glassy carbon electrode (GCE) were reduced through electrochemical method to form reduced graphene oxide (RGO)/PVB nanofibers. The morphology and structure of GO/PVB nanofiber were studied by scanning election mic...
متن کاملDosimetry characterization of nitro-blue tetrazolium polyvinyl butyral films for radiation processing
Nitro-blue tetrazolium polyvinyl butyral film dosimeters (NBT-PVB) were prepared and investigated based on radiation-induced reduction of NBT. NBT-PVB film dosimeters containing different concentrations of NBT dye from 1 to 5 mM were prepared in a solution of ethanol. The dosimeters were irradiated with g-ray from Co source at doses from 5 up to 55 kGy. UV/vis spectrophotometry was used to inve...
متن کامل