Microstructure and thermal history of metal particles in CH chondrites

available online at http://meteoritics.org Microstructure and thermal history of metal particles in CH chondrites J. I. GOLDSTEIN1*, R. H. JONES2, P. G. KOTULA3, and J. R. MICHAEL3 1Department of Mechanical and Industrial Engineering, 313 Engineering Laboratory, University of Massachusetts, 160 Governors Drive, Amherst, Massachusetts 01003, USA 2Department of Earth and Planetary Sciences, University of New Mexico, Albuquerque, New Mexico 87131, USA 3Materials Characterization Department, Sandia National Laboratories, P.O. Box 5800, M.S. 0886, Albuquerque, New Mexico 87185, USA *Corresponding author. E-mail: [email protected] (Received 30 August 2006; revision accepted 27 January 2007) Abstract–We have studied metal microstructures in four CH chondrites, Patuxent Range (PAT) 91546, Allan Hills (ALH) 85085, Acfer 214, and Northwest Africa (NWA) 739, to examine details of the thermal histories of individual particles. Four types of metal particles are common in all of these chondrites. Zoned and unzoned particles probably formed as condensates from a gas of chondritic composition in a monotonic cooling regime, as has been shown previously. We have demonstrated that these particles were cooled rapidly to temperatures below 500 K after they formed, and that condensation effectively closed around 700 K. Zoned and unzoned particles with exsolution precipitates, predominantly high-Ni taenite, have considerably more complex thermal histories. Precipitates grew in reheating episodes, but the details of the heating events vary among individual grains. Reheating temperatures are typically in the range 800–1000 K. Reheating could have been the result of impact events on the CH parent body. Some particles with precipitates may have been incorporated into chondrules, with further brief heating episodes taking place during chondrule formation. In addition to the four dominant types of metal particles, rare Ni-rich metal particles and Si-rich metal particles indicate that the metal assemblage in CH chondrites was a mixture of material that formed at different redox conditions. Metal in CH chondrites consists of a mechanical mixture of particles that underwent a variety of thermal histories prior to being assembled into the existing brecciated meteorites.We have studied metal microstructures in four CH chondrites, Patuxent Range (PAT) 91546, Allan Hills (ALH) 85085, Acfer 214, and Northwest Africa (NWA) 739, to examine details of the thermal histories of individual particles. Four types of metal particles are common in all of these chondrites. Zoned and unzoned particles probably formed as condensates from a gas of chondritic composition in a monotonic cooling regime, as has been shown previously. We have demonstrated that these particles were cooled rapidly to temperatures below 500 K after they formed, and that condensation effectively closed around 700 K. Zoned and unzoned particles with exsolution precipitates, predominantly high-Ni taenite, have considerably more complex thermal histories. Precipitates grew in reheating episodes, but the details of the heating events vary among individual grains. Reheating temperatures are typically in the range 800–1000 K. Reheating could have been the result of impact events on the CH parent body. Some particles with precipitates may have been incorporated into chondrules, with further brief heating episodes taking place during chondrule formation. In addition to the four dominant types of metal particles, rare Ni-rich metal particles and Si-rich metal particles indicate that the metal assemblage in CH chondrites was a mixture of material that formed at different redox conditions. Metal in CH chondrites consists of a mechanical mixture of particles that underwent a variety of thermal histories prior to being assembled into the existing brecciated meteorites.