Critical currents of ex situ YBa2Cu3O7− thin films on rolling assisted biaxially textured substrates: Thickness, field, and temperature dependencies
نویسندگان
چکیده
A. O. Ijaduola,1 J. R. Thompson,1,2 R. Feenstra,2 D. K. Christen,2 A. A. Gapud,2 and X. Song3 1Department of Physics, University of Tennessee, Knoxville, Tennessee 37996-1200, USA 2Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831-6061, USA 3Applied Superconductivity Center, University of Wisconsin, Madison, Wisconsin 53706-1390, USA Received 5 December 2005; revised manuscript received 3 March 2006; published 4 April 2006
منابع مشابه
Mechanisms of weak thickness dependence of the critical current density in strong-pinning ex situ metal–organic-deposition-route YBa2Cu3O7−x coated conductors
We report on the thickness dependence of the superconducting characteristics including critical current Ic, critical current density Jc, transition temperature Tc, irreversibility field Hirr, bulk pinning force plot Fp(H), and normal state resistivity curve ρ(T ) measured after successive ion milling of ∼1 μm thick high-Ic YBa2Cu3O7−x films made by an ex situ metal–organic deposition process on...
متن کاملIon-beam-assisted Deposition of Magnesium Oxide Films for Coated Conductors
The development of high critical-temperature thin-film superconductors and coated conducting wires is important for electric power applications. To achieve high transport current density, template films are necessary for the successful deposition of biaxially aligned YBa2Cu3O7-x (YBCO) on flexible metal substrates. We grew biaxially aligned magnesium oxide (MgO) template films by ion-beam-assis...
متن کاملCharacterization of highly-oriented ferroelectric PbxBa1−x TiO3 thin films grown by metalorganic chemical vapor deposition
PbxBa1−xTiO3 (0.2 x 1) thin films were deposited on single-crystal MgO as well as amorphous Si3N4/Si substrates using biaxially textured MgO buffer templates, grown by ion beam-assisted deposition (IBAD). The ferroelectric films were stoichiometric and highly oriented, with only (001) and (100) orientations evident in x-ray diffraction (XRD) scans. Films on biaxially textured templates had smal...
متن کاملGrowth and optical property characterization of textured barium titanate thin films for photonic applications
We have investigated the growth of barium titanate thin films on bulk crystalline and amorphous substrates utilizing biaxially oriented template layers. Ion beam-assisted deposition was used to grow thin, biaxially textured, magnesium oxide template layers on amorphous and silicon substrates. Growth of highly oriented barium titanate films on these template layers was achieved by molecular beam...
متن کاملProcessing Dependence of Texture, and Critical Properties of YBa2Cu3O7 d Films on RABiTS Substrates by a Non-Fluorine MOD Method
YBa2Cu3O7 d (YBCO or Y123) films on rolling-assisted biaxially textured substrates (RABiTS) were prepared via a fluorinefree metallorganic deposition (MOD) through spin coating, burnout, and high temperature anneal. The effects of substrate texture and surface energy of the CeO2 cap layer were investigated. Except for the commonly accepted key factors, such as the textures of substrate and buff...