Synthesis and Characterization of Bimagnetic Bricklike Nanoparticles
نویسندگان
چکیده
Bimagnetic FePt/CoFe2O4 nanoparticles having a bricklike morphology were synthesized by growing a soft magnetic CoFe2O4 phase on FePt cubic nanoparticle seeds. The size of the soft phase could be controlled by tuning the material ratio of the FePt seeds to the CoFe2O4 component. To obtain magnetic hardening, the as-synthesized bricklike nanoparticles were annealed at elevated temperatures under a reductive atmosphere to convert the disordered face-centered cubic FePt phase into the ordered L10 phase having high magnetic anisotropy. When the particles were annealed, a gradual change was observed in morphology from bricklike particles to spherical polycrystalline nanocomposite particles because of diffusion. Meanwhile, the magnetic energy density was enhanced as a result of the exchange coupling between the hard and soft phases. The enhancement was dependent on the ratio of the volumes of the soft phase and the hard phase.
منابع مشابه
Synthesis and Characterization of V2O5/SiO2 Nanoparticles as Efficient Catalyst for Aromatization 1,4 Dihydropyridines
V2O5/SiO2 nanoparticles was prepared via an one-pot sol gel method from vanadyl- acetylacetonate and tetraethylorthosilicate in refluxing MeOH, followed by calcination at 700 °C for 2 hours. The resultant nanoparticles was characterized by means of scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), TGA and FTIR techniques. Rapid and efficient ar...
متن کاملGreen Synthesis of Zinc Oxide Nanoparticles using Garlic skin extract and Its Characterization
Plant-mediated synthesis of metal oxide nanoparticles is a promising alternative to the traditional method of physical and chemical synthesis. In this paper, we report the green synthesis of zinc oxide nanoparticles (ZnONPs) by a biological method. During the study, Zinc oxide nanoparticles were synthesized by Allium sativum skin (garlic skin) extract. Formation of zinc oxide nanoparticles has ...
متن کاملSynthesis and characterization of SnO2 nanoparticles by Co-Precipitation method
Tin oxide (SnO2)nanoparticles were synthesized by co-precipitation method and the synthesized nanoparticles were annealed at different temperatures for characterization. The powders were investigated with X-ray diffraction, scanning electron microscopy and optical spectroscopy. The structural characterization was carried out by X-ray diffraction which confirms the crystalline nature ...
متن کاملControllable Synthesis of Silver Nanoparticles Using Citrate as Complexing Agent: Characterization of Nanopartciles and Effect of pH on Size and Crystallinity
A method for the controllable synthesis of silver nanoparticles based on a complexing agent method was developed. Citric acid was used as a complexing agent. The effect of pH (1.6 to 5.17) on the size and net height (as obtained from XRD analyses) of silver nanoparticles was investigated. The nanoparticles (10 to 40 nm) were characterized using XRD, TEM, SEM, EDX, UV-Vis spectrosco...
متن کاملCaF2 nanoparticles: Synthesis and characterization
The aim of the present study was to prepare nano-sized calcium fluoride (CaF2). Calcium fluoride nanoparticles were synthesized by CaCl2.6H2O and ammonium fluoride. Nanoparticles were synthesized by co-precipitation method. The synthesized nanocrystals were characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), scanning electro...
متن کامل