Thin Film Magnesium Boride Superconductor with Very High Critical Current Density and Enhanced Irreversibility Field
نویسنده
چکیده
Larbalestier †§ N. Rogado*, K.A. Regan*, M.A. Hayward*, T. He*, J.S. Slusky*, K. Inumaru*, M.K. Haas* and R.J. Cava* † Department of Materials Science and Engineering, Univer-sity of Wisconsin, 1509 University Avenue, Madison, WI 53706 USA § Applied Superconductivity Center, University of Wisconsin, 1500 Engineering Drive, Madison, WI 53706 USA * Department of Chemistry and Princeton Materials Institute, Princeton University, Princeton, NJ 08544 USA
منابع مشابه
As-grown Growth of MgB2 Thin Films and Fabrication of Josephson Junctions
In the fall of 2001, a group of researchers at Aoyama Gakuin University published a report in Nature on a new superconducting material, MgB2 (magnesium boride), which has a critical temperature of 39 K [1], the finding of which sent shock waves around the world. The discovery of superconductivity in Hg traces back to 1911. Since then, various metals and metal compounds have been confirmed to sh...
متن کاملA ug 2 00 1 Magnetic relaxation and critical current density of MgB 2 thin films
Magnetic relaxation and critical current density have been measured on a M gB 2 thin film in a wide region of temperature with the magnetic field up to 8 T. The irreversibility line has also been determined. It is found that the relaxation rate has a very weak temperature dependence below 1/2T c showing a clear residual relaxation rate at zero K, which cannot be easily explained as due to therm...
متن کاملPotential Application of Magnesium Diboride for Accelerator Magnet Applications*
This paper reviews the potential of the newly discovered and unexpected 39 K superconductor MgB2 as a material for accelerator magnet strands. Unlike the high temperature cuprate superconductors, intergranular current flow in MgB2 is not obstructed by weak links, removing one serious obstacle to the fabrication of wires. The critical current density Jc exceeds 10 5 A/cm in 1 T field at 4.2 K an...
متن کاملStrongly enhanced flux pinning in one-step deposition of BaFe2(As0.66P0.33)2 superconductor films with uniformly dispersed BaZrO3 nanoparticles
The high upper critical field and low anisotropy of the iron-based superconductor BaFe₂As₂ make it promising for its use in the construction of superconducting magnets. However, its critical current density in high magnetic fields needs to be improved. Here we demonstrate a simple, one-step and industrially scalable means of achieving just this. We show that introducing controlled amounts of un...
متن کاملEnhanced critical-current in P-doped BaFe2As2 thin films on metal substrates arising from poorly aligned grain boundaries
Thin films of the iron-based superconductor BaFe2(As1-xPx)2 (Ba122:P) were fabricated on polycrystalline metal-tape substrates with two kinds of in-plane grain boundary alignments (well aligned (4°) and poorly aligned (8°)) by pulsed laser deposition. The poorly aligned substrate is not applicable to cuprate-coated conductors because the in-plane alignment >4° results in exponential decay of th...
متن کامل