Patterned FeNi soft magnetic strips film with tunable resonance frequency from 1 to 10.6 GHz
نویسندگان
چکیده
Soft magnetic films with a wide-range tunable ferromagnetic resonance frequency are suitable for miniaturization and multifunctionalization of microwave integrated circuits. Fabrication of these films for high-frequency applications is usually complicated and difficult. We demonstrate a simple method to fabricate patterned FeNi soft magnetic strip films by magnetron sputtering and photolithography. Films prepared by this method exhibits a tunable in-plane uniaxial magnetic anisotropy (IPUMA) for different strip widths and gaps. As the strip widths changing from 500 to 2 μm, the IPUMA field increases monotonically from 2.2 to 576 Oe and resonance frequency from 1 to 10.6 GHz(which covers four microwave bands, including the L,S,C and X bands) respectively. This ultra-wide-range adjustability of resonance frequency can be attributed to shape anisotropy of strips. Considering that FeNi alloy has relatively low magnetocrystalline anisotropy, so a wider adjustable range of resonance frequency could be obtained using materials with stronger magnetocrystalline anisotropy.
منابع مشابه
EMC’04/Sendai RF ITEGRATED NOISE SUPPRESSOR ON CPW USING FERROMAGNETIC RESONANCE AND EDDY CURRENT LOSS
The RF integrated noise suppressor is demonstrated by integration of soft magnetic films on coplanar transmission line. Vertical structure is composed of the magnetic film (2 mm x 15 mm x 1, 2 m) /2 m-thick polyimide/15.2 mm-long and 3 mthick Cu transmission line/seed layer (Ti/Cu) /1 mm-thick glass substrate. The coplanar transmission line was prepared by electroplated Cu with 50 characteristi...
متن کاملDevelopment, fabrication and characterization of soft-magnetic thin films for high frequency applications
This submitted manuscript describes the development, fabrication and characterization of soft-magnetic thin films for high frequency applications up to GHz frequencies. These high frequency suitable films were investigated with the prospective use as magnetic core material, for the assembly of micro inductors or micro sensors for the micro electronic and micro system technology. Within the scop...
متن کاملHigh-Frequency Behavior and Damping of Fe–Co–N-Based High-Saturation Soft Magnetic Films
Magnetization dynamics measurements at subnanosecond time scale have been performed on Fe–Co–N high-saturation soft magnetic films with Permalloy nanolayer seeds and having a saturation magnetization of 1.9 MA/m (1900 emu/cm). The damping parameter varies from 0.011 to 0.018, depending on applied bias field. The peak frequencies of the imaginary permeability spectra and the zero-crossing freque...
متن کاملAdvanced Soft Magnetic Materials for Magnetic Recording Heads and Integrated Inductors
High performance magnetic heads, inductors and transformers, indispensable to information technology encompassing from information storage, portable power delivery, to wireless communication, require soft magnetic films with low coercivities, high permeability, and large ferromagnetic resonance frequencies. The Fe-Co-N-based films have a ferromagnetic resonance frequency of >1 GHz at zerobias f...
متن کاملElectronically tunable magnetic patch antennas with metal magnetic films
Introduction: Patch antennas on ferrites substrates showed tunable radiation frequency, polarisation diversity, and beam steering [1]. In addition, it was recently demonstrated that patch antennas on a selfbiased ferrite-dielectric composite substrate showed a miniaturisation factor of > 5, a 600% enhanced bandwidth and a high efficiency at a resonance frequency of 277 MHz [2]. The introduction...
متن کامل