Initial Bacterial Adhesion on Different Yttria-Stabilized Tetragonal Zirconia Implant Surfaces in Vitro

نویسندگان

  • Lamprini Karygianni
  • Andrea Jähnig
  • Stefanie Schienle
  • Falk Bernsmann
  • Erik Adolfsson
  • Ralf J. Kohal
  • Jérôme Chevalier
  • Elmar Hellwig
  • Ali Al-Ahmad
چکیده

Bacterial adhesion to implant biomaterials constitutes a virulence factor leading to biofilm formation, infection and treatment failure. The aim of this study was to examine the initial bacterial adhesion on different implant materials in vitro. Four implant biomaterials were incubated with Enterococcus faecalis, Staphylococcus aureus and Candida albicans for 2 h: 3 mol % yttria-stabilized tetragonal zirconia polycrystal surface (B1a), B1a with zirconium oxide (ZrO₂) coating (B2a), B1a with zirconia-based composite coating (B1b) and B1a with zirconia-based composite and ZrO₂ coatings (B2b). Bovine enamel slabs (BES) served as control. The adherent microorganisms were quantified and visualized using scanning electron microscopy (SEM); DAPI and live/dead staining. The lowest bacterial count of E. faecalis was detected on BES and the highest on B1a. The fewest vital C. albicans strains (42.22%) were detected on B2a surfaces, while most E. faecalis and S. aureus strains (approximately 80%) were vital overall. Compared to BES; coated and uncoated zirconia substrata exhibited no anti-adhesive properties. Further improvement of the material surface characteristics is essential.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

On the bulk degradation of yttria-stabilized nanocrystalline zirconia dental implant abutments: an electron backscatter diffraction study

Degradation of yttria-stabilized zirconia dental implants abutments due to the tetragonal to monoclinic phase transformation was studied in detail by microstructural characterization using Electron Back Scatter Diffraction (EBSD). The amount and distribution of the monoclinic phase, the grain-size distribution and crystallographic orientations between tetragonal and monoclinic crystals in 3 mol...

متن کامل

Investigation of the mechanical properties of various yttria stabilized zirconia based thin films prepared by aqueous tape casting

In this study various yttria doped  zirconia based thin films were prepared by the aqueous tape casting method. The rheological property of the paste was studies. The phase content and microstructure of the samples was investigated by X-ray diffraction and scanning electron microscope, respectively. The mechanical properties of thin films were studied by Vickers microhardness and nanoindentatio...

متن کامل

Vergleichende Untersuchungen zur Radioaktivität von Knochenzementen und der darin enthaltenen Röntgenkontrastmittel Studies to compare radioactivity of bone cements and their ingredient X-ray contrast media

There is interest in using zirconia for biomedical applications as ball heads for total hip prostheses. Two potential types are under discussion: partially stabilized zirconia (PSZ) and tetragonal zirconia polycrystals (TZP) materials. Because of its enhanced material properties, TZP stabilized with yttria is favourable. To eliminate high amounts of natural radioactive impurities, the precursor...

متن کامل

Abrasivity of Yttria Tetragonal Zirconia Polycrystals Abrasivity of Yttria Tetragonal Zirconia Polycrystal (Y-TZP) to dental enamel in comparison to Noble White High Palladium alloy

Objectives: To test the wear of enamel against Yttria Tetragonal Zirconia Polycrystals (Y-TZP) in comparison to the wear of enamel against a noble white high Palladium alloy. Methods: A total of 20 specimens were used, 10 of Y-TZP and 10 of High Palladium alloy, both were subjected to 202,800 contacts against an enamel rod 2x2 mm in cross section under a mean load of 475.04g leading to a mean f...

متن کامل

Characteristics of yttria stabilized tetragonal zirconia powder used in optical fiber connector ferrule

The tetragonal to monoclinic (t ! m) phase transformation during low temperature ( 100 8C) degradation (LTD) of yttria-stabilized tetragonal zirconia polycrystals (Y-TZP) sintered in air at different temperatures was investigated. It is found that the sintering temperature affected the density, crystalline phase and microstructure of the sintered body, as well as the LTD behavior. Also, the ons...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 6  شماره 

صفحات  -

تاریخ انتشار 2013