Preparation of delafossite CuFeO2 thin films by rf- sputtering on conventional glass substrate
نویسنده
چکیده
CuFeO2 is a delafossite-type compound and is a well known p-type semiconductor. The growth of delafossite CuFeO2 thin films on conventional glass substrate by radio-frequency sputtering is reported. The deposition, performed at room temperature leads to an amorphous phase with extremely low roughness and high density. The films consisted of a well crystallized delafossite CuFeO2 after heat treatment at 450 °C in inert atmosphere. The electrical conductivity of the film was 1 mS/cm. The direct optical band gap was estimated to be 2 eV.
منابع مشابه
The Effect of Substrate on Structural and Electrical Properties of Cu3N Thin Film by DC Reactive Magnetron Sputtering
The aim of this paper is to study the effect of substrate on the Cu3N thin films. At first Cu3N thin films are prepared using DC magnetron sputtering system. Then structural properties, surface roughness, and electrical resistance are studied using X-ray diffraction (XRD), the atomic force microscope (AFM) and four-point probe techniques respectively. Finally, the results are investigated and c...
متن کاملA Study of ZnO Buffer Layer Effect on Physical Properties of ITO Thin Films Deposited on Different Substrates
The improvement of the physical properties of Indium Tin Oxide (ITO) layers is quite advantageous in photovoltaic applications. In this study the ITO film is deposited by RF sputtering onto p-type crystalline silicon (c-Si) with (100) orientation, multicrystalline silicon (mc-Si), and glass substrates coated with ZnO and annealed in vacuum furnace at 400°C. Electrical, optical, structural a...
متن کاملEffect of Thickness on Properties of Copper Thin Films Growth on Glass by DC Planar Magnetron Sputtering
Copper thin films with nano-scale structure have numerous applications in modern technology. In this work, Cu thin films with different thicknesses from 50–220 nm have been deposited on glass substrate by DC magnetron sputtering technique at room temperature in pure Ar gas. The sputtering time was considered in 4, 8, 12 and 16 min, respectively. The thickness effect on the structural, mo...
متن کاملThe effect of sputtering RF power on structural, optical and electrical properties of CuO and CuO2 thin films
In this paper, the RF power change effect on the structural, optical and electrical properties of CuO thin films prepared by RF reactive magnetron sputtering deposited on glass substrates are studied. At first, the thin films are prepared at 150, 280, 310 and 340W respectively. Then, the films are characterized by XRD, AFM, Uv-visible and four-point probe analysis respectively. The results show...
متن کاملGa DOPED ZnO THIN FILMS DEPOSITED BY RF MAGNETRON SPUTTERING – PREPARATION AND PROPERTIES
Gallium doped zinc oxide, GZO, thin films have been deposited onto glass substrate by rf magnetron sputtering at various substrate temperatures. The electrical and optical properties of the thin films have been studied as a function of substrate temperature. X-ray diffraction was used in order to investigate thin film structures. The thin film structure was stabilised by heating the samples in ...
متن کامل