Acoustic Emission Wavelet Analysis of Filament Wound Composite Tube Fatigue Damage Process

نویسندگان

  • Su Hua
  • Chang Cheng
چکیده

This paper did a radial compression fatigue test on glass fiber winding composite tubes, collects acoustic emission signals on different fatigue damages stages, used time frequency analysis techniques of modern wavelet transform, and analyzed the wave form and frequency characteristics of fatigue damaged acoustic emission signals. Three main frequency bands of acoustic emission signal had been identified: 80-160 kHz (low frequency band), 160-300 kHz (middle frequency band), and over 300kHz (high frequency band), corresponding to the three basic damage modes: the fragmentation of matrix resin, the layered damage of fiber and matrix, and the fracture of cellosilk. The usage of wavelet transform enabled the separation of fatigue damaged acoustic emission signals from interference wave, and the access to characteristics of high signal-noise-ratio fatigue damage.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Flexural monitoring of carbon fiber/epoxy composite by acoustic emission

Carbon / epoxy composite is one of the most useful polymer matrix composites that has special properties such as high strength-to-weight ratio, high hardness, high corrosion resistance, Resistance to nuclear radiation has high consumption in different industries such as aerospace industry. Therefor monitoring of loading of this type of composite is important. In order to determine failure mecha...

متن کامل

Cluster Analysis of Acoustic Emission Signals for Carbon/Epoxy Composite in Four-point Bending Test (RESEARCH NOTE)

Due to the extensive use of composites in various industries and the fact that defects reduce ultimate strength and efficiency during operation, detection of failures in composite parts is very important. The aim of this paper is to use Acoustic Emission (AE) non-destructive method in four-point bending test of carbon/epoxy composite to analyze and examine the failure mechanisms. This method is...

متن کامل

Damage Energy Evaluation in [55/-55]9 Composite Pipes using Acoustic Emission Method

In this study, the longitudinal and hoop tensile strengths of an industrial ±55° Glass Reinforced Epoxy (GRE) pipe with eighteen layers as well as the associated failure mechanisms are determined. To obtain the longitudinal and hoop tensile strengths values, three specimens are cut from the studied GRE pipe in each direction. A comparison is done between both the strength values, and the fractu...

متن کامل

On the Use of Acoustic Emission and Digital Image Correlation for Welded Joints Damage Characterization

A series of tests have been conducted to investigate fatigue damage characterization in corroded welded steel plates using structural health monitoring (SHM) techniques. Acoustic Emission (AE) is a non-destructive testing (NDT) technique with potential applications for locating and monitoring fatigue cracks in service. In the present work, AE is implemented to characterize damage during crack e...

متن کامل

Reliability of the Rubber Tube of Automotive Hydraulic Braking System Under Fatigue Failures Considering Random Variation of Load and the Process of Aging of Material

This paper presents the approach for the assessing of the operational reliability of a multi-layer thick-walled tube made of rubber with textile reinforcement. The analysis of the fatigue accumulation process is carried out within the framework of the concept of the continuum mechanics of damage. The mathematical model, which takes into account the accumulation of damages in case of a random sp...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2015