Substrate-free, large-scale, free-standing and two-side oriented single crystal TiO2 nanorod array films with photocatalytic properties.
نویسندگان
چکیده
A substrate-free, large-scale, free-standing and two-side oriented single crystal rutile TiO(2) nanorod array film with a thickness of over ten micrometers, self-assembled via a facile hydrothermal reaction of titanium powder in a mixture solution of H(2)O(2) and HCl, exhibits high activity for the photocatalytic degradation of methyl orange.
منابع مشابه
نانومیله‌های نانوبرگ‌دار شده دی‌اکسید تیتانیم دوفازی به‌منظور استفاده در کاربردهای فتوالکتروشیمیایی
Rutile-phase titanium dioxide nanorod arrays were prepared by the hydrothermal method. Then, anatase-phase nanoleaves were successfully synthesized on the nanorod arrays via mild aqueous chemistry. Nanorod arrays scanning electron microscopy revealed that the thin film is uniform and crack free and the average diameter and height of the nanorods are 90 nm and 2 µm, respectively. Furthermo...
متن کاملAn illustration of photocatalytic properties of ZnO nanorods array films
ZnO nanorods array films were coated on a glass template through a two-step chemical process. First, a sol-gel spin coating method was used to produce a ZnO seed layer and after that, the ZnO nanorods arrays were grown on it through a low temperature aqueous method. Synthesized films were studied by scanning electron microscope (SEM) and X-ray diffractometer (XRD). X-ray diffraction results sho...
متن کاملSTUDY OF ANNEALING TEMPERATURE VARIATION ON THE STRUCTURAL PROPERTIES OF DIP-COATED TiO2-SiO2 NANOSTRUCTURED FILMS
Abstract:In the present research, SiO2–TiO2 nanostructure films were successfully prepared on windshields using the sol–gel technique for photocatalytic applications. To prevent the thermal diffusion of the sodium ions from the glass to TiO2 films, the SiO2 layer was pre-coated on the glass by the sol–gel method. The substrates were dipped in the sol and withdrawn with the speed of 6cm/min-1 to...
متن کاملAnatase TiO2 nanotube powder film with high crystallinity for enhanced photocatalytic performance
We report on the synthesis of TiO2 nanotube (NT) powders using anodic oxidation and ultrasonication. Compared to free-standing NT array films, the powder-type NTs can be easily fabricated in a cost-effective way. Particularly, without the substrate effect arising from underlying Ti metals, highly crystallized NT powders with intact tube structures and pure anatase phase can be obtained using hi...
متن کاملTransparent free-standing film of 1-D rutile/anatase TiO2 nanorod arrays by a one-step hydrothermal process.
Through the addition of a solid-state precursor, a large-scale, transparent, and free-standing film of 1-D rutile/anatase TiO2 nanorod arrays can be fabricated by dynamically changing the acidity and concentrations of titanium and chloride ions, and creating anatase growth-friendly conditions.
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Chemical communications
دوره 47 13 شماره
صفحات -
تاریخ انتشار 2011