Influence of synthesis temperature on morphology of SBA-16 mesoporous materials with a three-dimensional pore system
نویسندگان
چکیده
Influence of synthesis temperature on morphology of SBA-16 mesoporous materials with a three-dimensional pore system, Abstract Spherical particles of mesoporous silica SBA-16 with cubic Im3m structure were synthesized at low pH using Pluronic F127 as template and TEOS as silica source. The diameter of the spherical particles can be controlled in the range of 0.5 – 8 µm by varying synthesis temperature between 1 °C up to 40 °C. A sharp transition from large particle sizes at approximately 20 °C to smaller ones is observed when the temperature is increased. It is suggested that this morphology transition is due to a change in hydrolysis and condensation rate of the silica source and as a result the assembly of F127 micelles will differ. The SBA-16 samples were characterized using powder X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Nitrogen adsorption techniques.
منابع مشابه
Mesoporous silica SBA-15 sheet with perpendicular nanochannels.
Free-standing thin sheet form of mesoporous silica materials with perpendicular orientation is a much desired materials for its possible applications in catalysis, mask, and separation. A three component amphiphile system of sodium dodecyl sulfate/hexadecyltrimethylammonium bromide/pluronic-123(C(16)TMAB/SDS/P123) was employed to template the condensation of sodium silicates for the formation o...
متن کاملبررسی قابلیت جذب هیدروژن در ماده مرکب نانوساختار SBA-16-Pd
The purpose of this work was to study the hydrogen adsorption on the surface of mesoporous materials based on silica (SBA-16) modified with palladium via temperature. Since mesoporous silica materials have a high specific surface area, and the ordered mesoporous size of 2-10nm, they are suitable for adsorption and storage of hydrogen. SBA-16 is suitable for this purpose due to its cubic crystal...
متن کاملFunctionalized Mesoporous SBA-15 with CeF3: Eu3+ Nanoparticle by Three Different Methods: Synthesis, Characterization, and Photoluminescence
Luminescence functionalization of the ordered mesoporous SBA-15 silica is realized by depositing a CeF3: Eu3+ phosphor layer on its surface (denoted as CeF3: Eu3+/SBA-15/IS, CeF3: Eu3+/SBA-15/SI and CeF3: Eu3+/SBA-15/SS) using three different methods, which are reaction in situ (I-S), solution impregnation (S-I) and solid phase grinding synthesis (S-S), respectively. The structure, morphology, ...
متن کاملModification of mesoporous silica SBA-15 with different organic molecules to gain chemical sensors: a review
The recognition of the biologically and environmentally important ions is of great interest in the field of chemical sensors in recent years. The fluorescent sensors as a powerful optical analytical technique for the detection of low level of various analytes such as anions and metal cations have been progressively developed due to the simplicity, cost effective, and selectivity for monitoring ...
متن کاملSynthesis and Characterization of Amine-modified Mesoporous SBA-15 for Carbon Dioxide Sequestration at High Pressure and Room Temperature (RESEARCH NOTE)
Amine-modified mesoporous SBA-15 adsorbent has been prepared by impregnation method using tetraethylenepentamine. The samples of this modified SBA-15 have been characterized by small angle X-ray scattering (SAXS), Scanning electron microscopy (SEM), Nitrogen adsorption-desorption isotherm and FT-IR. The adsorption capacity of CO2 on unmodified and modified samples were measured at high pressure...